Sigma phase in the cast alloy based on the Fe3Al intermetallic phase

• Autorzy: Podrez-Radziszewska M. , Lachowicz M. , Haimann K. , Jasionowski R.
• Języki publikacji: EN

Abstrakty

EN

The paper presents study results for cast alloy based on the Fe3Al intermetallic phase. The study material was Fe-28Al-5Cr-1Mo-0,1Zr- 0,005B% at. alloy in the cast state. The microscopic research, phase analysis with X-ray diffraction, bending test and observation of the alloy surface exposed to corrosion have been performed. It has been found that presence of the sigma phase in the material structure influences high hardness of the tested alloy, its susceptibility to brittle fracture and favours the intercrystalline corrosion.

Słowa kluczowe

EN

metallography; sigma phase; intermetallic phase; brittleness

PL

metalografia; faza sigma; faza międzymetaliczna; kruchość krzepnięcia; korozja międzykrystaliczna

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2011
• Tom: Vol. 11, iss. 2
• Strony: 105--108
• Opis fizyczny: Bibliogr. 8 poz., rys., wykr.

Twórcy

autor

Podrez-Radziszewska M.

autor

Lachowicz M.

autor

Haimann K.

autor

Jasionowski R.

• Materials Science Division, Institute of Materials Science and Applied Mechanics, Wroclaw University of Technology, Smoluchowskiego 25, 50-372 Wrocław, Poland,

Bibliografia

• [1]. G. Bergman, D. P. Shoemaker: The determination of the crystal structure of the \sigma phase in the iron−chromium and iron−molybdenum systems. Acta Cryst. 7, (1954) 857.
• [2]. A. Błachowski: Wpływ domieszek, mikrostruktury i temperatury na kinetykę przemiany fazowej \alfa-\sigma w układzie Fe-Cr. Rozprawa doktorska, AGH Kraków 2000.
• [3]. A. Mikikits-Leitner, B. Sepiol, M. Leitner: Nucleation mechanism of the \sigma-to-\alfa phase transition in FeB1B−BxBCrBxB. Physical Review B 82 (2010), pp. 100101(1-4).
• [4]. http://www.geocities.jp/ohba_lab_ob_page/.
• [5]. K. Garbala, A. Patejuk: Welding technology of the intermetallic FeB3BAl phase. Archives of Foundry Engineering 10, special issue 1, (2010), pp. 459-462.
• [6]. R. Jasionowski, W. Przetakiewicz, D. Zasada: The effect of casting porosities on cavitational erosion of intermetallic alloy FeAl36. Archives of Foundry Engineering 10, issue 3, (2010), pp. 175-178.
• [7]. A. Patejuk: Influence of loading on wear of composite material FeAl-AlB2B0B3B. Archives of Foundry Engineering 7, issue 2, (2007), pp. 15-18.
• [8]. W. Szkliniarz, T. Mikuszewski: Wytwarzanie stopów na osnowie fazy międzymetalicznej FeAl metodami metalurgii próżniowej. Inżynieria Materiałowa 4-5, 2003, s. 155-159.