Optimising the composition of natural moulding sands including thermal aspects

• Autorzy: Kowalski J. S.
• Języki publikacji: EN

Abstrakty

EN

The paper discusses the problem of the choice of the moulding sand mixture composition in terms of the sand behaviour in contact with molten metal. Studies of high-temperature phenomena make assessment of the sand composition applicability under real operating conditions possible, thus leading to the elimination of sand-originating casting defects. The research was conducted on selected moulding materials included in the composition of traditional moulding sand mixtures without the addition of carbon. The effect of moulding sand composition and moisture content on the linear dilatation and stress-induced allotropic changes of quartz was examined. The analysis of these phenomena was based on 3D charts and maps generated from data collected during the tests.

Słowa kluczowe

EN

metal casting; moulding; moulding mixture; moulding sand

PL

odlewnictwo metali; formowanie; masa formierska; piasek formierski

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2011
• Tom: Vol. 11, iss. 2
• Strony: 65--68
• Opis fizyczny: Bibliogr. 6 poz., wykr.

Twórcy

autor

Kowalski J. S.

• Chair of Materials Technology, Institute of Materials Engineering, Cracow University of Technology, ul. Warszawska 24, 31-155 Kraków, Poland,

Bibliografia

• [1] Lewandowski L.: Tworzywa na formy odlewnicze. Wyd. "Akapit", Kraków, 1997.
• [2] Goerlich E.: Chemia krzemianów. Wyd. PWN Warszawa, 1973.
• [3] Baliński A. i in.: Komputerowa, trójwymiarowa ocena skłonności mas do tworzenia powierzchniowych wad odlewów. Opracowanie dla KBN, Instytut Odlewnictwa, Kraków, 1995.
• [4] Dietert H.: Badania mas formierskich i rdzeniowych w podwyższonych temperaturach i ich związek z jakością odlewów. Foundry, t. 102, 1957.
• [5] Henschel C.: Casting Dimension and Mold Dilatation. Mod. Casting, t. 50, 1966.
• [6] Poźniak P.: Rola wybranych parametrów materiałów formierskich w procesach temperaturowych mas formierskich. Praca dyplomowa inżynierska, promotor - dr inż. Jerzy St. Kowalski, PK Kraków, 2007.