Aluminide protective coatings on high-temperature creep resistant cast steel

• Autorzy: Kubicki J. , Kochmańska A.
• Języki publikacji: EN

Abstrakty

EN

This paper presents the results of research on aluminide protective coatings manufactured on high-temperature creep resistant cast steel. The main purpose of these coatings is protection against the high temperature corrosion, especially at high carburizing potential atmosphere. Coatings were obtained on cast steel type G-XNiCrSi36-18 with the following methods: pack cementation, paste method, cast method and slurry cementation. The phase composition, thickness and morphology of coatings were determined. Coatings capacity of carbon diffusion inhibition and thermal shocks resistance of coatings were determined with different methods. It was found, that all of the coatings reduce carbon diffusion in different degree and all coatings liable to degradation in consequence cracking and oxidation. Coating life time is mainly dependent on morphology, phase composition and service condition (thermal shocks first of all).

Słowa kluczowe

EN

anticarburizing protective coatings; pack cementation; cast method; paste method; slurry method; thermal shocks

PL

antynawęglanie; powłoka ochronna; metoda zawiesinowa; szok termiczny

• Wydawca: Komisja Odlewnictwa Polskiej Akademii Nauk Oddział w Katowicach
• Czasopismo: Archives of Foundry Engineering
• Rocznik: 2009
• Tom: Vol. 9, iss. 4
• Strony: 113--124
• Opis fizyczny: Bibliogr. 20 poz., rys., tab., wykr.

Twórcy

autor

Kubicki J.

autor

Kochmańska A.

• West Pomeranian University of Technology in Szczecin, Piastów 19, 70-310 Szczecin, Poland,

Bibliografia

• [1] Lai G. Y. Heat-resistant materials for furnace parts, Trays and Fixtures, ASM Handbook - Heat Treating, vol. 4, 510-524.
• [2] Grabke H. J., Wolf L. Carburization and Oxidation. Material Science Engineering No 87 (1987) 23-28.
• [3] Hocking M. G., Vasantasree V., Sidky P. S. Metallic and ceramic coatings, Longman Scientic & Technical, UK, (1989).
• [4] Wang, K.-L., Chen, F.-S., Leu, G.-S., The aluminizing and Al-Si codeposition on AISI HP alloy and the evaluation of their carburizing resistance, Material Science and Engineering, A 357 (2003) 27-38.
• [5] Houngninou C., Chevalier S., Larpin J. P. Synthesis and characterization of pack cemented aluminide coatings on metals, Applied Surface Science, No 236 (2004) 256-269.
• [6] Swadźba L., Mendala B., Hetmańczyk M. Degradation of aluminide, chromium-aluminide and thermal barier coatings of cyclic thermal and mechanical loads, European Federation of Corrosion Publications, No 27 (1999).
• [7] Christodulu P.: Doctor Thesis, Szczecin, 1984.
• [8] Christodulu P., Piekarski B.: Schutz von G-XNiCrSi 37.17- Stahlgup mittels eines Al-Cu- Uberzugs vorden Auswirkungen aufkohlender Atmosphare, NEUE HUTTE No.5 (1986) 192-196.
• [9] Piekarski B.: Odlewy ze staliwa austenitycznego w budowie pieców do nawęglania. Teoretyczne i praktyczne aspekty podwyższania trwałości, Prace Naukowe Politechniki Szczecińskiej, No 573, Szczecin 2003.
• [10] Borisow W. T., Borisow W. I. Primienienie EBM dlja izućenija kinetiki rosta sloev pri gieterofaznoj diffuzii. Zašč. Pokr. Metall. No.11 (1977) 24-28.
• [11] Garbiak M., Drotlew A., Kubicki J., Piekarski B. Anticarburising coatings for castings operating under the condisions of thermal shocks, Przegląd Odlewnictwa, No 9 (2004) 742-751.
• [12] Piekarski B., Kubicki J. Ochrana lite oceli 36%Ni/18%Cr povlekanfm na bazi hliniku pred vlivem atmosfery nasycene uhlikem. Slevarenstwi No.4 (2002) 140-144.
• [13] Kubicki J.: Odlewnicze powłoki Al-Cu na staliwie żarowytrzymałym, Prace Naukowe Politechniki Szczecińskiej, No 529, Szczecin 1996.
• [14] Kubicki J., Piekarski B. Aluminium protective coatings produced on creep-resisting steel directly in a casting mould, Metalurgija No.4 (2003) 223-228.
• [15] Xiang Z. D., Datta P. K. Codeposition of Al and Si on nickel base superalloys by pack cementation process, Material Science Engineering, No A356 (2003) 136.
• [16] Kochmańska A., Kubicki J.: Multilayer and multicomponent Al-Si coatings, Acta Metallurgica Slovaca, Special Issue 1 (2004) s. 943-946.
• [17] Kubicki J., Kochmańska A.: Powłoki ochronne Al-Si otrzymane metodą zawiesinową, Mat. Konf. Współpraca'05, AGH, Zakopane (2005) s. 119-124.
• [18] Kochmańska A., Kubicki J., Kochmański P., Lenart S.: Wpływ parametrów wytwarzania na strukturę powłok ochronnych Al-Si otrzymanych metodą zawiesinową, Inżynieria Materiałowa 5 (2005) s. 728-730.
• [19] Kochmańska A.: Antynawęgleniowe powłoki otrzymane metodą zawiesinową o podwyższonej odporności na wstrząsy cieplne, Inżynieria Materiałowa 6 (2008) s. 679-682.
• [20] Kochmańska A., Kubicki J. Efficiency of protective coatings on high creep resistant cast steel, Archives of Foundry Engineering, w druku (2009).