Monolithic La1-xPtxMnO3 and LaMn1-xPtxO3 perovskite catalysts for the oxidation of methane and carbon oxide

• Autorzy: Kucharczyk B. , Zabrzeski J.

Warianty tytułu

PL

Monolityczne katalizatory perowskitowe LaMnO3 z dodatkiem platyny w utlenianiu metanu i monotlenku węgla

• Języki publikacji: EN

Abstrakty

EN

The substitution of 0.1-0.2 mol of lanthanum in LaMnO3 by platinum enhances the activity of the perovskite in CO oxidation, and the La0.9Pt0.1MnO3-based catalyst was found to be most active in this process. When the CO oxidation involves the temperatures higher than 270 ?C, the catalysts based on LaMn0.9Pt0.1O3, La0.8Pt0.2MnO3 and La0.85Pt0.15MnO3 perovskites do not differ in activity. In CH4 combustion, the La0.9Pt0.1MnO3 and LaMn0.9Pt0.1O3 catalysts display a higher activity than the LaMnO3 catalyst does. When the Pt content in LaMnO3 is higher than 0.1, its activity in CH4 combustion and the resistance to thermal shocks decrease. When some part of La in the LaMnO3 perovskite is substituted by Pt, the specific surface area of the perovskite decreases from 8.6 m2/g (LaMnO3) to 3.1 m2/g (La0.8Pt0.2MnO3).

PL

eśli w perowskicie LaMnO3 zastąpić od 0,1 do 0,2 mola lantanu platyną, to zwiększa się aktywność tego perowskitu w utlenianiu CO. Najwyższą aktywność w utlenianiu wykazuje katalizator z perowskitem La0,9Pt0,1MnO3. Metan jest efektywniej utleniany, gdy 0,1 mola lantanu w katalizatorze LaMnO3 zastępuje się platyną. Większa zawartość platyny w perowskicie LaMnO3 obniża zarówno jego aktywność w utlenianiu CO, jak i odporność katalizatora perowskitowego na naprzemienne zmiany temperatury. Zastąpienie części lantanu w perowskicie LaMnO3 platyną zmniejsza powierzchnię właściwą perowskitu z 8,58 m2/g (LaMnO3) do 3,1 m2/g (La0,8Pt0,2MnO3).

Słowa kluczowe

EN

platinium; perovskite; catalysts; catalysis; oxidation; catalyst activity

PL

platyna; kataliza; katalizatory; perowskit; utlenianie; aktywność katalizatora

• Wydawca: Oficyna Wydawnicza Politechniki Wrocławskiej
• Czasopismo: Environment Protection Engineering
• Rocznik: 2008
• Tom: Vol. 34, nr 4
• Strony: 75--80
• Opis fizyczny: bibliogr.8 poz.

Twórcy

autor

Kucharczyk B.

autor

Zabrzeski J.

• Institute of Inorganic Technology and Mineral Fertilizers, Wrocław University of Technology, Wybrzeże Wyspiańskiego 27, 50-370 Wrocław,

Bibliografia

• [1] GELIN P., PRIMET M., Complete oxidation of methane at low temperature over noble metal based catalyst: a review, Appl. Catal. B, 2002, Vol. 39, 1.
• [2] MUSIALIK-PIOTROWSKA A., KOYER-GOŁKOWSKI A., Porównanie aktywności katalizatorów perowskitowego i palladowego w utlenianiu organicznych zanieczyszczeń powietrza, Ochrona Środowiska, 2002, 2(85), 7.
• [3] CIMINO S., PIRONE R., LISI L., Zirconia supported LaMnO3 monoliths for the catalytic combustion of methane, Appl. Catal. B: Environ., 2002, Vol. 35, 243.
• [4] CIAMBELLI P., CISINO S., ROSSI S., LISI L., MINELLI G., PORTA P., RUSSO G., AFeO3 (A = La, Nd, Sm) and LaFe1-xMgxO3 perovskites as methane combustion and CO oxidation catalysts: structural, redox and catalytic properties, Appl. Catal. B, 2001, Vol. 29, 239.
• [5] SONG K., CUI H.X., KIM S.D., KANG S., Catalytic combustion of CH4 and CO on La1-xMxMnO3 perovskites, Catal. Today, 1999, Vol. 47, 155.
• [6] TANAKA H., MIZUNO N., MISONO M., Catalytic activity and structural stability of La0.9Ce0.1 Co1–xFexO3 perovskite catalysts for automotive emissions control, Appl. Catal. A, 2003, Vol. 244, 371.
• [7] ZHOU K., CHEN H., TIAN Q., HAO Z., SHEN D., XU X., Pd-containing perovskite-type oxides used for three-way catalysts, J. Mol. Catal. A., 2002, Vol. 189, 23.
• [8] POCOROBA E., JOHANSSON E.M., JARAS S.G., Ageing of palladium, platinum and manganese-based combustion catalysts for biogas applications, Catal. Today, 2000, Vol. 59, 179.