CuO as sintering additive to Sr0.4Ca0.6La4Ti5O17 ceramics

• Autorzy: Manan A. , Shah L. A. , Attaullah
• Języki publikacji: EN

Abstrakty

EN

The effects of CuO addition on the sintering behavior and microwave dielectric properties of Sr0:4Ca0:6La4Ti5O17 ceramics were investigated. CuO was selected as a liquid phase sintering aid to lower the sintering temperature of Sr0:4Ca0:6La4Ti5O17 ceramics. With CuO addition, the sintering temperature of Sr0:4Ca0:6La4Ti5O17 ceramics was effectively reduced from 1550 °C to 1475 °C. The crystalline phase exhibited no phase difference and no second phase was detected at all addition levels. The electric permittivity was not significantly affected by various amounts of CuO addition and ranged from 52 to 54. Small values (<+7 ppm/K) of the temperature coeficient of resonant frequency were obtained for Sr0:4Ca0:6La4Ti5O17 ceramics. However, the unloaded quality factor Qu was strongly dependent upon the CuO concentration. Qu fo - 10500 GHz was obtained for Sr0:4Ca0:6La4Ti5O17 ceramics with 0.5 wt.% of CuO addition, sintered at 1475 °C.

Słowa kluczowe

EN

CuO; calcination; additive

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2013
• Tom: Vol. 31, No. 1
• Strony: 122--125
• Opis fizyczny: Bibliogr. 16 poz., rys., wykr.

Twórcy

autor

Manan A.

autor

Shah L. A.

autor

Attaullah

• Department of Physics, University of Science and Technology Bannu, Postcode 28100, Pakistan

Bibliografia

• [1] OUCHI H., KAWASHIMA S., Jpn. J. Appl. Phys., 24 (2) (1985), 60.
• [2] WAKINO K., NISHIKAWA T., ISHIKAWA Y., TAMURA H., Br. Ceram. Trans., 39 (1990), 89.
• [3] SREEMOOLANADHAN H., SEBASTIAN M.T., MOHANAN P., Mater. Res. Bull., 30 (6) (1995), 653.
• [4] OVCHAR O., DURYLIN D., BELOUS A., JANCAR B., KOLODIAZHNYI., Mater. Sci. Poland., 29 (1) (2011), 56.
• [5] KIM D.W., KIM J.R., YOON S.H., HONG K.S., KIM C.K., J. Am. Ceram. Soc., 85 (11) (2002), 2759.
• [6] LIM J.B., JEONG Y.H., NGUYEN N.H., NAHM S., PAIK J.H., KIM J.H., LEE H.J., J. Eur. Ceram. Soc., 27 (2007), 2875.
• [7] TZOU W.C., YANG C.F., CHEN Y.C., CHENG P.S., J. Eur. Ceram. Soc., 20 (2000), 991.
• [8] KANG D.H., NAM K.C., CHA H.J., J. Eur. Ceram. Soc., 21 (2006), 1726.
• [9] JACOB M.V., PAMU D., RAJU K.C.J., J. Am. Ceram. Soc., 90 (5) (2007), 1511.
• [10] JAWAHAR I.N., SANTHA N., SEBASTIAN M.T., J. Mater. Res., 17(2002), 3084.
• [11] ZHAO Z., YUE Z., GUI, LI L., J. Am. Ceram. Soc., 89 (11) (2006), 3421.
• [12] CHEN Y.C., TSAI J.M., Jpn. J. Appl. Phys., 47 (2008), 7959.
• [13] IQBAL Y., MANAN A., REANEY I.M., Mater. Res. Bull., 46 (7) (2011), 1092.
• [14] KRUPKA J., DERZAKOWSKI K., RIDDLE B., JARVIS J.B., Meas. Sci. Technol., 9 (1998), 1751.
• [15] SHANNAN R.D., Acta Cryst. A32, (1976), 751.
• [16] WU L., YANG C.F.T.S., WU T.S., J. Mater. Sci. Mater. Electron., 3 (1992), 272.