Structural and dielectric properties of La substituted polycrystalline Ca(Ti0.5Fe0.5)O3

• Autorzy: Shah M. R. , Akther Hossain A. K. M.
• Języki publikacji: EN

Abstrakty

EN

Polycrystalline Ca1xLax(Ti0:5Fe0:5)O3 were prepared by the standard solid state reaction technique. Pellet shaped samples prepared from each composition were sintered at 1573 K for 5 h. The X-ray diffraction analysis indicated the formation of a single-phase orthorhombic structure. The lattice parameters as well as densities increased but the average grain sizes decreased with the increase of La content. The dielectric measurements were carried out at room temperature as a function of frequency and composition. The experimental results revealed that dielectric constant (e0) decreased but dielectric loss (tand) and ac electrical conductivity (sac) increased as frequency increased. The composition dependence of e0 and tand indicated that they decreased with the increase of La content. The sac was derived from the dielectric measurements and it is concluded that the conduction in the present samples is due to mixed polarons hopping.

Słowa kluczowe

EN

ceramics; chemical synthesis; X-ray diffraction; dielectric properties

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2013
• Tom: Vol. 31, No. 1
• Strony: 80--87
• Opis fizyczny: Bibliogr. 13 poz., rys., wykr.

Twórcy

autor

Shah M. R.

autor

Akther Hossain A. K. M.

• Department of Physics, Primeasia University, Banani, Dhaka-1213, Bangladesh

Bibliografia

• [1] GOODENOUGH J.B., Rep. Prog. Phys., 67 (2004), 1915.
• [2] JONES R.E., MAINAR P.D., OLOWOLAFE J.O., CAMPBELL J.O., MOGAB C.J., Appl. Phys. Lett., 60 (1992), 1022.
• [3] SETTER N. et al., J. Appl. Phys., 100 (2006), 051606.
• [4] CARREAUD J., BOGICEVIC C., DKHIL B., KIAT J.M.,Appl. Phys. Lett., 92 (2008), 242902.
• [5] KIM B.G., CHO S.M., KIM T.Y., JANG H.M., Phys. Rev. Lett., 86 (2001), 3404.
• [6] GUO Y., KAKIMOTO K., OHSATO H., Solid State Commun., 129 (2004), 279.
• [7] SHI J.,YANG W., J. Alloys Compd., 472 (2009), 267.
• [8] RAMIREZ A.P. et al., Solid State Commun., 115 (2000),217.
• [9] WU J., NAN C. W., LIN Y. H., DENG Y., Phys. Rev.Lett., 89 (2002), 217601.
• [10] FU M.S., LIU X.Q., CHEN X.M., J. Eur. Cer. Soc., 28(2008), 585.
• [11] YOON K.H., KIM W.S., KIM E.S., Mater. Sci. Eng. B,99 (2003), 112.
• [12] CHUNG C.Y., CHANG Y.H., CHANG Y.S., CHEN G.J.,J. Alloys Compd., 385 (2004), 298.
• [13] MENDELSON M.I., J. Am. Ceram. Soc., 52 (8) (1969),443.