Influence of stearic acid on the structure and rheological behavior of injection-molded ZTA suspensions

• Autorzy: Lin C. , Wang B. , Cheng Y. , Wang C.
• Języki publikacji: EN

Abstrakty

EN

The zirconia-toughened-alumina (ZTA) composite powder was exposed to a prior ball milling treatment with a small amount of stearic acid (SA) before the traditional blending process. The effect of different amounts of stearic acid on surface properties of the powder, the particle size distribution of the powder, and the rheological properties of the suspension were systematically studied within the design of experiments. Fourier transformation infrared spectroscopy (FTIR) analysis was used to prove the chemical interaction between the stearic acid and the ZTA powder. The effects of SA content on the particle sizes and their distribution were carefully examined. Rheological properties such as viscosity, yield stress, and power law exponent of the suspensions were determined within a temperature range of 140-170 °C. The optimal content of SA to improve the properties of the suspensions was found to be 3 wt.%.

Słowa kluczowe

EN

ZTA suspension; ceramic injection moulding; rheological property

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2013
• Tom: Vol. 31, No. 1
• Strony: 36--42
• Opis fizyczny: Bibliogr. 24 poz., rys., wykr.

Twórcy

autor

Lin C.

autor

Wang B.

autor

Cheng Y.

autor

Wang C.

• Institute of Materials Science and Engineering, Fuzhou University, Fujian, China, 350108

Bibliografia

• [1] ATTARIAN M., NASSAJ E.T., DAVAMI P.,Ceram. Int., 128 (2002), 507.
• [2] LIU D.M., J. Eur. Ceram. Soc., 82 (1999), 1162.
• [3] XIE Z.P., LUO J.S., WANG X., LI J.B., HUANG Y., Mater. Des., 26 (2005), 79.
• [4] LIU W., XIE Z.P., JIA C., J. Eur. Ceram. Soc., 32 (2012), 1001.
• [5] NOVAK S., VIDOVI K., SAJKO M., KOSMA T., J. Eur. Ceram. Soc., 17 (1997), 217.
• [6] HANEMANN T., HELDELE R.,Int. J. Appl. Ceram. Technol., 8 (2011), 1296.
• [7] HANEMANN T.,Composites Part A, 37 (2006), 735.
• [8] SUPATI R., LOH N.H., KHOR K.A., TOR S.B., Mater. Lett., 46 (2000), 109.
• [9] TSENG W.J., Mater. Sci. Eng. A, 289 (2000), 116.
• [10] TSENG W.J., LIU D.M., HSU C.K., Ceram. Int., 25 (1999), 191.42 CONG LIN et al.
• [11] LIU D.M., TSENG W.J., J. Eur. Ceram. Soc., 82 (1999), 2647.
• [12] LI Y.M., LIU X.Q., LUO F.H., YUE J.L., Trans. Nonferrous Met. Soc. China., 17 (2007), 1.
• [13] HANEMANN T., HELDELE R., MUELLER T., HAUSSELT J., Int. J. Appl. Ceram. Technol., 8 (2011), 865.
• [14] BARD. Y., Non-linear Parameter Estimation and Programming, IBM, New York, 1967.
• [15] LIU W., XIE Z.P., YANG X.F., WU Y., JIA C., BO T.Z., WANG L.L., J. Eur. Ceram. Soc., 94 (2011), 1327.
• [16] LIU W., XIE Z.P., BO T.Z., YANG X.F., J. Eur. Ceram. Soc., 31 (2011), 1611.
• [17] WEI W.C.J., TSAI S.J., HSU K.C., J. Eur. Ceram. Soc., 18 (1998), 1445.
• [18] LIU D.M., TSENG W.J., J. Eur. Ceram. Soc., 35 (2000), 1009.
• [19] CETINEL F.A., BAUER W., MULLER ¨ M., KNITTER R., HAUSSELT J., J. Eur. Ceram. Soc., 30 (2010), 1391.
• [20] EDIRISINGHE M.J., SHOW H.M., TOMKINS K.L., Ceram. Int., 18 (1992), 193.
• [21] TRUNEC M., HRAZDERA J., Ceram. Int., 31 (2005), 845.
• [22] SOTOMAYOR M.E., VAREZ ´ A., LEVENFELDS B., Powder Technol., 200 (2010), 30.
• [23] LIU D.M., TSENG W.J., Mater. Sci. Eng. A, 254 (1998), 136.
• [24] LIU D.M.,Ceram. Int., 25 (1999), 587.