Thermal Properties of Functionalised Metallocene Polypropylene Fibres

• Autorzy: Kristofic M. M. , Ujhelyiova A. , Ryba J.

Warianty tytułu

PL

Właściwości termiczne modyfikowanych metalocenowych włókien polipropylenowych

• Języki publikacji: EN

Abstrakty

EN

In this contribution blend metallocene polypropylene (mPP) fibres modified with 4, 8, 12 wt.% of copolyamide A and 4, 8, 12 wt.% of compatibiliser L were prepared. Copolyamide A consists of 85 wt.% of e-caprolactam and 15 wt.% of nylon salt of adipic acid and diethylenetriamine. Compatibiliser L is low molecular isotactic polypropylene grafted with maleineanhydride. Thermal properties of the components, blends and modified mPP fibres were evaluated. Fibres modified with both copolyamide A and compatibilizer were successfully spun and drawn, with the opposite being the case for mPP fibres modified only with copolyamide A without compatibiliser L, which were not spun, confirming the positive role of compatibiliser L. The modified fibres conserve their thermal characteristics - melting temperature, melting enthalpy and entropy in the whole interval of both additive concentrations evaluated. The positive influence of the compatibiliser was found from the point of melting enthalpy and melting entropy.

PL

Przygotowano dla oceny włókna wykonane z mieszanek metalocenowanego polipropylenu modyfikowanego 4, 8 i 12% kopoliamidem A oraz 4, 8 i 12% kompatybilizatorem L. Kopoliamid A składa si. z 85% e-kaprolaktamu i 15% soli nylonowej kwasu adypinowego i dietylenotriaminy. Kompatybilizator L jest niskomolekularnym izotaktycznym polipropylenem szczepionym bezwodnikiem maleinowym. Oceniono właściwości termiczne składników i gotowych produktow. Z polimerow z zastosowaniem kompatybilizatora z łatwością wyprzędziono włókna, podczas gdy mieszanki polimerów bez udziału kompatybilizatora nie dały się prząść. Dla otrzymanych włókien analizowano temperaturę topnienia, entalpię i entropię dla całego zakresu stosowanych stężeń. Potwierdzono pozytywny wpływ zastosowanego kompatybilizatora.

Słowa kluczowe

EN

metallocene polypropylene; copolyamide; compatibilizer; modification; thermal properties; modified polypropylene fibres

PL

metalocenowe włókna; polipropylenowye; kompatybilizator; modyfikacja; właściwości termiczne; zmodyfikowane włókna polipropylenowe

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2012
• Tom: Vol. 20, no. 4 (93)
• Strony: 24--29
• Opis fizyczny: Bibliogr. 13 poz.

Twórcy

autor

Kristofic M. M.

autor

Ujhelyiova A.

autor

Ryba J.

• Slovakia, Bratislava, FCHPT, STU in Bratislava, Institute of Polymer Materials,, Department of Fibres and Textile Chemistry

Bibliografia

• 1. Krištofič M, Marcinčin A, Ujhelyiová A, Prchal V. Blended Fibre-Forming Polymer System PP/Polyamideurea III. Properties of Modified PP Fibres. Vlákna a textil (Fibres and Textiles) 1997; 4, 1: 14-17.
• 2. Krištofič M, Ujhelyiová A. PA 6, Copolyamides of ε-caprolactam with Nylon Salt of diethylene triamine + Adipic acid and their Thermal Properties. Fibres and Textiles in Eastern Europe 2006; 14, 4(58): 22-24.
• 3. Krištofič M, Náčiniaková Z, Legéň J, Ryba J. Polypropylene fibres modified by copolyamides. Part I. Preparation of modifiers, modified fibres and their properties. Vlákna a textil (Fibres and Textiles) 2005; 12, 3: 104-110.
• 4. Krištofič M, Hricová M, Ujhelyiová A. Modification of PP Fibres with Alkaline Copolyamides. Macromol. Symp. 2001; 170: 291-299.
• 5. Krištofič M. Modified Polypropylene Fibres. Fibres & Textiles in Eastern Europe 1994; 2, 2 (5): 38-39.
• 6. Yongsok Seo, Jinho Kim, Kwang Ung Kim and Young Chul Kim. Polymer 2000; 41: 2639-2646.
• 7. Kilwon Cho, Fengkui Li, Jaesung Choi. Crystallization and melting behaviour of blends polypropylene and maleated polypropylene blends. Polymer 1999; 40: 1719-1729.
• 8. Roeder J, Oliveira RVB, Gonçalves M, Soldi V, Pires ATN. Polymer Testing 2002; 21, 7: 815-821.
• 9. Gnatowski A, Koszkul J. Investigations of the influence of compatibilizer and filler type on the properties of chosen polymer blends. J. Mat. Process Technol 2005; 162-163: 52-58.
• 10. Campoy I, Arribas JM, Zaporta MAM, Marco C, Gómez MA, Fatou JG. Crystallization kinetics of polypropylene-polya-mide compatibilized blends. European Polymer J. 1995; 31, 5: 475-480.
• 11. Material of Clariant GmbH: Licomont – Specialities for Plastic Processing a Licomont AR 504, Division Pigments and Additives, BU Plastic Industire, MS Processors, 86005 Augsburg, Germany, (www.clariant.com).
• 12. Krištofič M, Ujhelyiová A, Ryba J. Structuralization and functionalization of fibre-forming metallocene polypropylene. Vlákna a textil (Fibres and Textiles) 2008; 15, 2-3: 3-8.
• 13. Krištofič M, Marcinčin A, Ujhelyiová A. The DSC Study of PA 6, Polyamides and Copolyamides. J. Therm Anal Cal 2000; 60: 357-369.