Coaxial Electrospinning of Miscible PLLA-Core and PDLLA-Shell Solutions and Indirect Visualisation of the Core-Shell Fibres Obtained

• Autorzy: Kriel H. , Sanderson R. D. , Smit E.

Warianty tytułu

PL

Współosiowe elektroprzędzenie roztworowe włókien o rdzeniu z PLLA i otoczce z PDLLA oraz ich wizualizacja

• Języki publikacji: EN

Abstrakty

EN

Core-shell fibres of semi-crystalline poly(L-lactic acid) (PLLA) (core) and amorphous poly(D,L-lactic acid) (PDLLA) (shell) were produced through the coaxial electrospinning of two miscible solutions. Due to the poor contrast between the PDLLA and PLLA, the core-shell structure of the resulting fibres could not be elucidated using TEM. An indirect visualisation method was devised consisting of a combination of SEM, selective dissolution, polarimetry and DSC. The method is evaluated here and applied in the investigation of the effect of spin solution concentration and flow rate on the morphology of the resulting fibers.

PL

W procesie współosiowego elektroprzędzenia uzyskiwano włókna typu rdzeń-otoczka stosując roztwory ulegające mieszaniu. Na rdzeń stosowano roztwory częściowo krystalicznego poli-(L-kwasu mlekowego), a na otoczkę roztwory amorficzne poli-(D,L-kwasu mlekowego). W wyniku nieznacznych różnic pomiędzy dwoma roztworami nie można było dokonać oceny techniką TEM. Zastosowano pośrednia metodę identyfikacji przy użyciu SEM, selektywnej rozpuszczalności, polarymetrii, różnicowej kalorymetrii skaningowej (DSC). Badano wpływ stężenia roztworów i szybkości ich podawania na morfologię otrzymywanych włókien.

Słowa kluczowe

EN

coaxial electrospinning; core-shell; poly(lactic acid)

PL

proces współosiowego elektroprzędzenia; poli(D,L-kwasu mlekowego); wpływ stężenia roztworów

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2012
• Tom: Vol. 20, no. 2 (91)
• Strony: 28--33
• Opis fizyczny: Bibliogr. 18 poz.,

Twórcy

autor

Kriel H.

autor

Sanderson R. D.

autor

Smit E.

• South Africa, Matieland, Stellenbosch University, Department of Chemistry and Polymer Science

Bibliografia

• 1. Moghe, A.K.; Gupta, B.S., Polymer Reviews, 2008, 48(2), 353-377.
• 2. Sun, Z. et al. Advanced Materials, 2003, 15, 1929-1932.
• 3. Zhang, Y. et al. Chemistry of Materials, 2004, 16, 3406-3409.
• 4. Yu, J.H.; Fridrikh, S.V.; Rutledge, G.C. Advanced Materials, 2004, 16, 1562-1566.
• 5. Li, D. Xia, Y. Nano Letters, 2004, 4(5), 933-938.
• 6. Li D., et al., Advanced Materials, 2004, 16, 2062-2066.
• 7. Li, D., McCann, J.T.; Xia, Y.; Small 1(1), 2005, 83-86.
• 8. Huang, Z-m., Zhang, Y., Ramakrishna, S. Journal of Polymer Science: Part B: Polymer Physics, 2005, 43, 2852–2861.
• 9. Jiang, H. et al. Journal of Controlled Release, 2005, 108, 237-243.
• 10. Wang, M. et al. Macromolecules, 2006, 39, 1102-1107.
• 11. Barkoula, N.-M. et al., Polymer Composites, 2005, 26, 114-120.
• 12. Li, R.; Yao, D. Journal of Applied Polymer Science, 2007, 107(5), 2909-2916.
• 13. Yao, D.; Li, R., Nagarajan, P. Polymer Engineering & Science, 2006, 46(9), 1223-1230.
• 14. Malherbe, I.; Sanderson, R.D.; Smit, E. Polymer, 2010, 51,5037-5043.
• 15. Wang, C. et al., Macromolecules, 2010, 43, 6389-6397.
• 16. Smit, A.E.; Sanderson; R.D. PCT International Patent Application PCT/2008/062264, 2008, May 29.
• 17. Garlotta, D. Journal of Polymers and the Environment, 2002, 9(2), 63-84.
• 18. Sarasua, J. et al. Journal of Materials Science, 2005, 40, 1855-1862.