Microwave dielectric properties of BiFeO3 multiferoic films deposited on conductive layers

• Autorzy: Sobiestianskas R. , Vengalis B. , Banys J. , Devenson J. , Oginskis A. K. , Lisauskas V. , Dapkus L.
• Języki publikacji: EN

Abstrakty

EN

Nondoped BiFeO3 (BFO) and doped Bi0.9La0.1Fe0.9Mn0.1O3 (BLFMO) thin films (d = 200-350 nm) were grown at 650- 750 °C by RF sputtering on Si and SrTiO3(100), coated by conductive LaNiO3 films and La2/3Ca1/3MnO3/SrRuO3 bilayers. The complex dielectric permittivity of the films was measured at room temperature in the frequency range from 10 MHz to 10 GHz using parallel plate capacitor structures. Dielectric properties of the polycrystalline BFO films were compared with those of the epitaxial quality BLFMO films, and it was seen that the latter has better microwave performance than the former. The dielectric losses were below 0.05 at 1 GHz frequency, which may be acceptable for microwave applications.

Słowa kluczowe

EN

multiferroic; bismuth ferrite; rf sputtering; dielectric permittivity; dielectric loss

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2011
• Tom: Vol. 29, No. 1
• Strony: 41--46
• Opis fizyczny: Bibliogr. 14 poz.,

Twórcy

autor

Sobiestianskas R.

autor

Vengalis B.

autor

Banys J.

autor

Devenson J.

autor

Oginskis A. K.

autor

Lisauskas V.

autor

Dapkus L.

• Vilnius University Faculty of Physics Sauletekio 9 Vilnius Lithuania

Bibliografia

• [1] FIEBIG M., J. Phys. D, 38 (2005), R123.
• [2] SMOLENSKII G.A., CHUPIS I.E., Sov. Phys. Usp., 25(1982), 475
• [3] WANG J., NEATON J.B., ZHENG H., NAGARAJAN V., OGALE S.B., LIU B., VEHLAND D.,VAITHYANATHAN V., SCHLOM D.G., WAGHMARE U.V., SPALDIN N.A., RABE K.M., WUTTIG M., RAMESH R., Science, 299 (2003), 1719.
• [4] YUAN G. L., ORA S. W., LIU J. M., LIU Z.G., Appl.Phys. Lett., 89 (2006), 052905.
• [5] YU B., LI M., LIU J., GUO D., PEI L., ZHAO X., J.Appl. Phys., 41 (2008), 06503.
• [6] TAKAHASHI K., KIDA N., TONOUCHI M., Phys. Rev.Lett., 96 (2006), 117402.
• [7] CHEN J.-C., WU J.-M., Appl. Phys. Lett., 91 (2007),182903.
• [8] ZHANG X-Y., SONG Q., XU F., ONG C.K., Appl.Phys. Lett., 94 (2009), 022907.
• [9] KAMBA S., NUZHNYY D., SAVINOV M., Sˇ EBEK J.,PETZELT J., PROKLESKA ˇ J., HAUMONT R., Phys. Rev.B., 75 (2007), 024403.
• [10] QI X., DHO J., TOMOV R., BLAMIRE M.G., MACMANUS-DRISCOL J.L., Appl. Phys.Lett., 86 (2005),062903.
• [11] MA Z., BECKER A.J., POLAKOS P., HUGGINS H.,PASTALAN J., WU H., WATTS K., WONG Y.H.,MANKIEWICH P., IEEE Trans. Electron Devices, 45(1998), 1811.
• [12] SOBIESTIANSKAS R., VENGALIS B., BANYS J., Proc.IEEE 18thIntl. Symp. Applications of Ferroelectrics ISAF 2009, Xian, China, 2009, p.232.
• [13] LANCASTER M.J., POWELL J., PORCH A., Supercond.Sci. Technol., 11 (1998), 1323.
• [14] KRAINIK N.N., KHUCHUA N.P., ZHDANOVA V.V., EVSEEV V.A., Sov. Phys. Solid State, 8 (1966), 654.