Thermal degradation of solvent-borne water soluble acrylic acid-butyl acrylate copolymers

Autorzy
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Thermal degradation of water soluble copolymers synthesized from acrylic acid and butyl acrylate, used as water soluble self-adhesives, especially for bonding of different kinds of paper, was investigated at 250 °C using pyrolysis-gas chromatography. The thermal degradation process and the kind and amounts of the pyrolysis products provide relevant information about the thermal resistance of water soluble acrylic adhesives. It was observed that during the pyrolysis of acrylic acid-butyl acrylate copolymers main breakdown products as carbon dioxide, butene-1, butanol-1, butyl acrylate and butyl methacrylate were formed.
Wydawca
Rocznik
Strony
851--856
Opis fizyczny
Bibliogr. 5 poz.
Twórcy
autor
autor
  • Institute of Chemical Organic Technology, Szczecin University of Technology, Pułaskiego 10, 70-322 Szczecin, Poland
Bibliografia
  • [1] MILKER R., CZECH Z., New trends and applications for water soluble PSAs, Conference AFERA, Brussels, Belgium, 2002.
  • [2] MILKER R., CZECH Z., Adhäsion, 6 (1989), 20.
  • [3] MILKER R., CZECH Z., Coating, 7 (2004), 275.
  • [4] D’HAESE F.C., LILLY J.V., Int. Patent WO 93/06184, Pressure-sensitive adhesion composition which is repulpable under acidic pH-conditions, 3M, 1992.
  • [5] LATTIMER R.P., J. Anal. Appl. Pyrolysis, 68–69 (2003), 3.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW7-0011-0139
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.