Thermal degradation of solvent-borne water soluble acrylic acid-butyl acrylate copolymers

• Autorzy: Czech Z. , Pełech R.
• Języki publikacji: EN

Abstrakty

EN

Thermal degradation of water soluble copolymers synthesized from acrylic acid and butyl acrylate, used as water soluble self-adhesives, especially for bonding of different kinds of paper, was investigated at 250 °C using pyrolysis-gas chromatography. The thermal degradation process and the kind and amounts of the pyrolysis products provide relevant information about the thermal resistance of water soluble acrylic adhesives. It was observed that during the pyrolysis of acrylic acid-butyl acrylate copolymers main breakdown products as carbon dioxide, butene-1, butanol-1, butyl acrylate and butyl methacrylate were formed.

Słowa kluczowe

EN

adhesion; pressure-sensitive adhesive; thermal resistance; thermal degradation products

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2009
• Tom: Vol. 27, No. 3
• Strony: 851--856
• Opis fizyczny: Bibliogr. 5 poz.

Twórcy

autor

Czech Z.

autor

Pełech R.

• Institute of Chemical Organic Technology, Szczecin University of Technology, Pułaskiego 10, 70-322 Szczecin, Poland

Bibliografia

• [1] MILKER R., CZECH Z., New trends and applications for water soluble PSAs, Conference AFERA, Brussels, Belgium, 2002.
• [2] MILKER R., CZECH Z., Adhäsion, 6 (1989), 20.
• [3] MILKER R., CZECH Z., Coating, 7 (2004), 275.
• [4] D’HAESE F.C., LILLY J.V., Int. Patent WO 93/06184, Pressure-sensitive adhesion composition which is repulpable under acidic pH-conditions, 3M, 1992.
• [5] LATTIMER R.P., J. Anal. Appl. Pyrolysis, 68–69 (2003), 3.