Tytuł artykułu

Hydrothermal synthesis of aqueous nano-TiO2 sols

Autorzy
Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
A poorly crystalline nano-anatase precursor with the crystallite sizes of about 3.5 nm was prepared via reprecipitation of nano-anatase at pH = 7.0 from a highly transparent sol obtained by acidic peptization of hydrous titania precipitates, hydrolysed product of titanium isopropoxide. The weakly agglomerated nano-anatase precursor has been used for preparing well crystalline nano-TiO2 sols by hydrothermal treatment at pH = 9.5 using a weak base, NH4OH. The crystallite size gradually grew with increasing temperature and reached 7.6 nm (X-ray) at 175 °C after 4 h of hydrothermal treatment. The sizes of particles were mostly in the range 5-15 nm. The hydroxyl content in the nano-TiO2 decreased with increasing hydrothermal temperature of treatment and supported a gradual growth of nano-TiO2 as evident from the X-ray and TEM.
Słowa kluczowe
Wydawca
Rocznik
Strony
465--470
Opis fizyczny
Bibliogr. 14 poz.
Twórcy
autor
autor
  • Sol-Gel Division, Central Glass and Ceramic Research Institute, 196, Raja S. C. Mullick Road, Kolkata 700 032, India
Bibliografia
  • [1] RINCON A.G., PULGARIN C., Appl. Catal. B: Environmental, 51 (2004), 283.
  • [2] SO C.M., CHENG M.Y., YU J.C., WONG P.K., Chemosphere, 46 (2002), 905.
  • [3] MATTHEWS R.W., J. Catal., 122 (1988), 549.
  • [4] ARUNA S.T., TIROSH S., ZABAN A., J. Mater. Chem., 10 (2000), 2388.
  • [5] YANG J., MEI S., FERREIRA J.M.F., J. Amer. Ceram. Soc., 83 (2000), 1361.
  • [6] YANG J., MEI S., FERREIRA J.M.F., J. Mater. Res., 17 (2002), 2197.
  • [7] HAYASHI H., TORII K., J. Mater. Chem., 12 (2002), 3671.
  • [8] KOLEN’KO Y.V., BURUKHIN A.A., CHURAGULOV B.R., OLEYNIKOV N.N., Mater. Lett., 57 (2003), 1124.
  • [9] BACSA R.R., GRATZEL M.L., J. Amer. Ceram. Soc., 79 (1996), 2185.
  • [10] ERDURAL B.K., YURUM A., BAKIR U., KARAKUS G., J. Nanosci. Nanotechnol., 8 (2008), 878.
  • [11] CHEN X., CHENG H., MA J., Powder Technol., 99 (1998), 171.
  • [12] PAIKE V.V., NIPHADKAR P.S., BOKADE V.V., JOSHI P.N., J. Amer. Ceram. Soc., 90 (2007), 3009.
  • [13] YOLDAS B.E., J. Mater. Sci., 21 (1986), 1087.
  • [14] ZHANG R., GAO L., Mater. Res. Bull., 36 (2001), 1957.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW7-0011-0101
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.