Preparation and characterization of yttria stabilized zirconia minispheres by the sol-gel drop generation method

• Autorzy: Judes J. , Kamaraj V.
• Języki publikacji: EN

Abstrakty

EN

Near-net-shaped zirconia minispheres were prepared by a novel processing technique based on the sol-gel method. Yttrium was used as a stabilizing agent. Formation of minispheres was achieved in a setting solution by drop generation. The impact of the stabilizing agent on sintering conditions was analysed in detail. The spheres were crystallized into tetragonal phase at 472 °C, and the tetragonal phase was retained up to 900 °C. Maximum theoretical density (97%) was achieved for spheres sintered at 900 °C. Sintering temperatures higher than 900 °C led to the formation of monoclinic phase and reduction in density. The grain size and crystallite size were identified as 0.8 žm and 24 nm, respectively. The phase identification, density variation, chemical decomposition, functional group specification and microstructural features of the dried and sintered final product were also studied.

Słowa kluczowe

EN

sol-gel method; zirconia minispheres; sintering; X-ray diffraction; thermal analysis

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2009
• Tom: Vol. 27, No. 2
• Strony: 407--415
• Opis fizyczny: Bibliogr. 21 poz.

Twórcy

autor

Judes J.

autor

Kamaraj V.

• Department of Ceramic Technology, Anna University, Chennai - 600025, India

Bibliografia

• [1] RUIZ L., READEY M.J., J. Am. Ceram. Soc., 79 (1996), 2331.
• [2] SETTU T., Studies on preparation and characterization of tetragonal zirconia polycrystals by sol-gel method, Ph. D. Thesis, Anna University, Chennai, India, 1995.
• [3] PANDOFELLI V.C., RODRIGUES J.A., STEVENS R., J. Mater. Sci., 26 (1991), 5327.
• [4] WANG J.A., VALENZUELA M.A., Catalysis Today, 68 (2001), 21.
• [5] VASYLKIV O., SAKKA Y., J. Am. Ceram. Soc., 83 (2000), 2196.
• [6] WANG H.C., LIN K.L., J. Mater. Sci., 26 (1991), 2501.
• [7] PULLAR R.C., TAYLOR M.D., BHATTACHARYA A.K., J. Eur. Ceram. Soc., 21 (2001), 19.
• [8] FULRATH R.M., PARK J.A., Ceramic Microstructures, Wiley, New York, 1968.
• [9] KUNDA P., PAL D., SEN S., J. Mater. Sci., 23 (1988), 1539.
• [10] MERCERA P.D.L., VAN OMMEN J.G., DOESBURG E.B.M., BURGGRAAF A.J., ROSS J.R.H., Appl. Catal., 57 (1990), 127.
• [11] NAUER M., Microstructure et superplasticite de Zircones Yittriées These No. 996, Departement des Materiux, Ecole Polytechnique Fédérale de Lausanne, Switzerland, 1992.
• [12] SRINIVASAN R., RICE L., DAVIS B.H., J. Am. Ceram. Soc., 73 (1990), 3528.
• [13] SRINIVASAN R., DAVIS B.H., CAVIN O.B., HUBBARD R., J. Am. Ceram. Soc., 75 (1992), 1217.
• [14] RAMADASS N., MOHAN S.C., RAVINDRA REDDY S., SRINIVASAN R., SAMDANI G., Mater Sci. Eng., 60 (1983), 65.
• [15] SCOTT H.G., J. Mater. Sci., 10 (1975), 1527.
• [16] GARVIE R.C., HANNINK R.H., PASCOE R.T., Nature, 258 (1975), 703.
• [17] DING J., TSUZUKI T., MCCORMICK P. Nanostruct. Mater., 8 (1997), 75.
• [18] ETIENNE J., LARBOT A., GRIZRAD C., COT.L., ALARY.I.A., J.Non-Cryst. Solids., 125 (1990), 224.
• [19] KHARITONOV Y.Y., ZAITSEV L.M., BOCHKAREW G.S., EVSTAFEVA O.N., Russ. J. Inorg. Chem., 9 (1964), 876.
• [20] GANGADEVI T., SUBBA RAO M., NARAYANAN KUTTY T.R., Ind. J. Chem., A19 (1980), 303.
• [21] INGEL R.P., LEWIS III D., J. Am. Ceram. Soc., 69(4) (1986), 325.