The effect of electromagnetic stirring on the microstructure and corrosion of mischmetal modified AZ91D magnesium alloy

• Autorzy: Jin Y. X. , Hua L. , Xu X. , Peng Q.
• Języki publikacji: EN

Abstrakty

EN

The microstructure and corrosion behaviour of mischmetal modified AZ91D magnesium alloy in the presence or absence of a rotating electromagnetic field have been investigated. The study suggests that the size and volume fraction of the ? (Mg17Al12) phase in the alloy decreases as magnetic field intensity increases. The immersion test results show that the mass loss for the alloy solidified in the absence of a magnetic filed is always larger than that for the alloy solidified under magnetic field. The electrochemical corrosion experiments indicate that the corrosion potential of the alloys increases from -1.56 to -1.51 V, while the corrosion current density decreases from 6.31 to 1.58 mAocm-2, and the charge transfer resistance increases from 3.17 to 11.32 k?ocm2 as the excitation voltage increases from 0 to 120 V. The enhancement of the corrosion resistance is attributed to the grain refinement, and to the volume fraction reduction of the ? (Mg17Al12) phase under a rotating electromagnetic field.

Słowa kluczowe

EN

microstructure; corrosion; magnesium alloy; mischmetal

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2009
• Tom: Vol. 27, No. 1
• Strony: 171--185
• Opis fizyczny: Bibliogr. 20 poz.

Twórcy

autor

Jin Y. X.

autor

Hua L.

autor

Xu X.

autor

Peng Q.

• School of Materials Science and Engineering, Taiyuan University of Technology, 030024 Taiyuan PR China

Bibliografia

• [1] HUTCHINSON C.R., NIE J.F., GORSSE S., Metall. Mater. Trans., A 36 (2005), 2093.
• [2] WABUSSEG H., GULLO G.C., UGGOWITZER P.J., STEINHOFF K., KAUFMANN H., J. Mater. Sci., 37 (2002), 1173.
• [3] SONG Y.L., LIU Y.H., YU S.R., ZHU X.Y., WANG S.H., J. Mater. Sci., 42 (2007), 4425.
• [4] WAN Y., TAN J., SONG G.L., YAN C.W., Metall. Mater. Trans., A 37 (2006), 2313.
• [5] MATHIEU S., RAPIN C., HAZAN J., STEINMETZ P., Corrosion Sci., 44 (2002), 2737.
• [6] STJOHN D.H., QIAN M., EASTON M.A., CAO P., HILDEBRAND Z., Metall. Mater. Trans., A 36 (2005), 1669.
• [7] YAO X.D., DAHLE A.K., DAVIDSON C.J., STJOHN D.H., J. Mater. Sci., 42 (2007), 9756.
• [8] TAMURA Y., KIDA1 Y., TAMEHIRO H., KONO N., SODA H., MCLEAN A., J. Mater. Sci., 43 (2008), 1249.
• [9] WANG Q.D., CHEN W.Z., DING W.J., ZHU Y.P., MABUCHI M., Metall. Mater. Trans., A 32 (2001), 787.
• [10] RAVI M., PILLAI U.T.S., PAI B.C., DAMODARAN A.D., DWARAKADASA E.S., Metall. Mater. Trans., A 27 (1996), 1283.
• [11] GUO S.J., LE Q.C., HAN Y., ZHAO Z.H., CUI J.Z., Metall. Mater. Trans., A 37 (2006), 3715.
• [12] DONG J., CUI J.Z., YU F.X., BAN C.Y., ZHAO Z.H., Metall. Mater. Trans., A 35 (2004), 2487.
• [13] MING X.G., BAO W.P., CUI J.Z., ZUO Y.B., Trans. Nonferrous Met. Soc. China, 13 (2003), 1270.
• [14] MIZUTANI Y., KAWATA J., MIWA K., YASUE K., TAMURA T., SAKAGUCHI Y., J. Mater. Res., 19 (2004), 2997.
• [15] EMADI D., GRUZLESKI J.E., TOGURI J.M., Metall. Mater. Trans., A 24 (1993), 1055.
• [16] CLOSSET B., GRUZLESKI J.E., Metall. Mater. Trans., A 13 (1982), 945.
• [17] GAO Y.L., LI Q.S., GONG Y.Y., ZHAI Q.J., Mater. Lett., 61 (2007), 4011.
• [18] FANG C.F., ZHANG X.G., JI S.H., HAO H., JIN J.Z., Rare Metal Mater. Eng., 36 (2007), 170.
• [19] HAMANA D., BOUCHEAR M., DERAFA A., Mater. Chem. Phys., 57 (1998), 99.
• [20] DUAN H.Q., WANG S.L., CAI Q.Z., ZHANG S.C., WEI B.K., China Mech. Eng., 14 (2003), 1789.