Structure and crystallization kinetics of amorphous Al-Ni-Si alloy

• Autorzy: Gögebakan M. , Okumus M.
• Języki publikacji: EN

Abstrakty

EN

In the present work, the structure and crystallization kinetics of rapidly solidified Al70Ni13Si17 amorphous alloy have been investigated by a combination of differential scanning calorimetry (DSC) and X-ray diffractometry (XRD). Amorphous ribbons were obtained by melt spinning at wheel speeds higher than 10 m/s. Crystallization of amorphous Al70Ni13Si17 alloy during continuous heating in DSC, takes places in three stages: (1) formation of fcc-Al and hexagonal phases; (2) growth of fcc-Al and hexagonal phases; (3) formation of fcc-Si and orthorhombic Al3Ni phases. Isothermal annealing DSC traces for this amorphous alloy, the first crystallization peak showed a clear incubation period, and the Avrami time exponent n has been determined to be 2.4-2.8 using the Johnson-Melh-Avrami analysis. This suggested that the transformation reaction involved continuous nucleation and three dimensional diffusioncontrolled growth. Electrical resistivity of the alloy was measured as 33x10-6 ? cm for the amorphous structure and 1x10-6 ? cm for the crystalline one. This study describes the structure and crystallization kinetics of a rapidly solidified Al70Ni13Si17 amorphous alloy.

Słowa kluczowe

EN

amorphous alloys; rapid solidification; X-ray diffraction; calorimetry

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2009
• Tom: Vol. 27, No. 1
• Strony: 79--87
• Opis fizyczny: Bibliogr. 16 poz.

Twórcy

autor

Gögebakan M.

autor

Okumus M.

• Department of Physics, Faculty of Art and Science, Kahramanmaras Sutcu Imam University,Kahramanmaras, 46000, Turkey

Bibliografia

• [1] KIM Y.H., HIRAGA K., INOUE A., MASUMOTO T. , JO H.H., Mater. Trans. JIM., 35 (1994), 293.
• [2] KIM Y.H., INOUE A. , MASUMOTO T., Mater. Trans. JIM., 31 (1990), 747.
• [3] CHANG I.T.H., BOTTEN R.R., Mater. Sci. Eng. A, 226-228 (1997), 183.
• [4] KIM W.T., GOGEBAKAN M., CANTOR B., Mater. Sci. Eng. A, 226–228 (1997),178.
• [5] GÖGEBAKAN M., UZUN O., KARAASLAN T., KESKIN M., J. Mater. Proc. Techno., 142 (2003), 87.
• [6] MUNOZ-MORRIS M.A., SURINACH S., GICH M., BARO M.D., MORRIS D.G., Acta Mater., 51 (2003), 1067.
• [7] GANGOPADHYAY A.K., KELTON K.F., Philos. Mag. A, 80 (2000), 1193.
• [8] BASSIM N., KIMINAMI C.S., KAUFMAN M.J., OLIVEIRA M.F., PERDIGÃO M.N.R.V., BOTTA FILHO W.J., Mater. Sci. Eng. A, 304–306 (2001), 332.
• [9] GLORIANT T., PING D.H., HONO K., GREER A.L., BARO M.D., Mater. Sci. Eng. A, 304–306 (2001), 315.
• [10] HONG S.J., WARREN P.J., CHUN B.S., Mater. Sci. Eng. A, 304–306 (2001), 362.
• [11] MCKAY B.J., CIZEK P., SCHUMACHER P., O’REILLY K.A.Q., Mater. Sci. Eng. A, 304–306 (2001), 240.
• [12] KISSINGER H.E., Anal. Chem., 29 (1957), 1702.
• [13] CHRISTIAN J.W., The Theory of Transformation in Metals and Alloys, Pergamon Press, Oxford, UK, 1975.
• [14] GÖGEBAKAN M., WARREN P.J., CANTOR B., Mater. Sci. Eng. A, 226–228 (1997), 168.
• [15] SCHUMACHER P., Nucleation in Aluminium Alloys Studied Using Devitrifation, Ph.D. Thesis, University of Cambridge, Cambridge, UK, 1993.
• [16] LEGRESY J.M., Characterization and Kinetics of the Crystallization of Al–Ni–Si Amorphous Alloys, Ph.D. Thesis, Institut National Polytechnique de Grenoble, 1987.