Nanocrystalline LiNi1-xCoxVO4 (x = 0.00, 0.25, 0.50, 0.75 and 1.00) was prepared from Li2CO3, Ni(NO3)2.6H2O, Co(NO3)2.6H2O and NH4VO3, using tartaric acid as a complexing agent, followed by 450 °C calcination for 12 h. TGA results show that nanocrystallites started to form at 450-550 °C. Inverse spinel LiNi1-xCoxVO4 was detected using the XRD and SAED methods. The calculated lattice parameter increased upon increasing Co concentration. It was in accordance with the increase in the particle size determined using TEM images. A stretching band of VO4 tetrahedra was detected at 651-820 cm-1 using FTIR. V-O vibrational bands analyzed with a Raman spectrometer were shifted to the lower wavenumbers, due to the increase of Co concentration. The selected elements were also analyzed using EDX and AAS to determine the stoichiometric values (x) of the oxides.
Słowa kluczowe
Wydawca
Czasopismo
Rocznik
Tom
Strony
43--49
Opis fizyczny
Bibliogr. 12 poz.
Twórcy
autor
autor
autor
- PERCH-CIC, Department of Chemistry, Faculty of Science, Chiang Mai University, Chiang Mai 50200, Thailand
Bibliografia
- [1] VIVEKANANDHAN S., VENKATESWARLU M., SATYANARAYANA N., Mater. Chem. Phys., 91 (2005), 54.
- [2] CHEN W., MAI L.Q., XU Q., ZHU Q.Y., YANG H.P., Mater. Sci. Eng., B 100 (2003), 221.
- [3] FEY G.T.K., HUANG D.L., Electrochim. Acta, 45 (1999), 295.
- [4] JULIEN C., MASSOT M., PÉREZ-VICENTE C., Mater. Sci. Eng., B 75 (2000), 6.
- [5] PRABAHARAN S.R.S., MICHAEL M.S., IKUTA H., UCHIMOTO Y., WAKIHARA M., Solid State Ion., 172 (2004), 39.
- [6] Powder Diffract. File, JCPDS Int. Centre Diffract. Data, PA 19073–3273, U.S.A., 2001.
- [7] KALYANI P., KALAISELVI N., MUNIYANDI N., Mater. Chem. Phys., 77 (2002), 662.
- [8] SURYANARAYANA C., NORTON M.G., X-Ray Diffraction, Plenum Press, New York, 1998.
- [9] BHUVANESWARI M.S., SELVASEKARAPANDIAN S., KAMISHIMA O., KAWAMURA J., HATTORI T., J. Power Source, 139 (2005), 279.
- [10] LAI Q.Y., LU J.Z., LIANG X.L., YAN F.Y., JI X.Y., Inter. J. Inorg. Mater., 3 (2001), 381.
- [11] LIU J.R., WANG M., LIN X., YIN D.C., HUANG W.D., J. Power Source, 108 (2002), 113.
- [12] ANDREWS K.W., DYSON D.J., KEOWN S.R., Interpretation of Electron Diffraction Patterns, Plenum Press, New York, 1971.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW7-0011-0061