Structure, magnetic and electrical transport properties of Mn4-xAgxN compounds

Identyfikatory
Warianty tytułu
Języki publikacji
EN
Abstrakty
EN
Mn4-xAgxN compounds (x = 0.0, 0.3, 0.6, 1.0) were prepared by milling and subsequently annealing the mixture of Mn2N0.86, Mn, and Ag powders. All compounds display good single-phase characteristics. Both Mn4N and Mn3.7Ag0.3N exhibit ferrimagnetism, and a little Ag replacement of Mn can improve the saturation magnetization. The magnetic transition of Mn3.4Ag0.6N and Mn3AgN below 15 K is from triangular antiferromagnetism to non-coplanar ferrimagnetism, while the ones at 256 and 275 K (Mn3.4Ag0.6N and Mn3AgN, respectively) have been ascribed to the gradual transition, as temperature increases, from the triangular antiferromagnetic structure T5g to a ferrimagnetic-like one. Two minima appear on the p(T) curves for Mn3AgN, with the observation of a positive magnetoresistance throughout the whole tempeature-dependent change.
Wydawca
Rocznik
Strony
33--42
Opis fizyczny
Bibliogr. 19 poz.
Twórcy
autor
autor
autor
autor
autor
autor
  • Shenyang National Laboratory for Materials Science, Institute of Metal Research, and International Centre for Materials Physics, Chinese Academy of SciencesShenyang 110015, China
Bibliografia
  • [1] BOUCHAUD J.P., Ann. Chim., 3 (1968), 81.
  • [2] KIM W.S., CHI E.O., HUR N.H., LEE K.W., CHOI Y.N., Phys. Rev. B, 68 (2003), 172402.
  • [3] CHI E.O., KIM W.S., HUR N.H., Solid State Commun., 120 (2001), 307.
  • [4] FENG W.J., LI D., REN W.J., LI Y.B., LI W.F., LI J., ZHANG Y.Q., ZHANG Z.D., J. Alloy. Compd., 437 (2007), 27.
  • [5] MAH A.D., J. Am. Chem. Soc., 80 (1958), 2954.
  • [6] TAKEI W.J., SHIRANE G., FRAZER B.C., Phys. Rev., 119(1) (1960), 122.
  • [7] TAKEI W.J., HEIKES R.R., SHIRANE G., Phys. Rev., 125(6) (1962), 1893.
  • [8] VEMPAIRE D., FRUCHART D., GOUTTEBARRON R., HLIL E.K., MIRAGLIA S., ORTEGA L., PELLETIER J., Physica A, 358 (2005), 136.
  • [9] FRUCHART D., BERTAUT E.F., J. Phys. Soc. Jpn., 44(3) (1978), 781.
  • [10] GOMONAJ E.V., L’VOV V.A., Phase Trans., 40 (1992), 225.
  • [11] NAVARRO R., ROJO J.A., GARCÍA J.J., GONZÁLEZ D., BARTOLOMÉ J., L’HERITIER PH., J. Magn. Magn. Mater., 59 (1986), 221.
  • [12] TAKENAKA K., TAKAGI H., Appl. Phys. Lett., 87 (2005), 261902.
  • [13] TAKENAKA K., TAKAGI H., Mater. Trans., 47 (3) (2006), 471.
  • [14] FENG W.J., SUN N.K., GAO M., ZHANG Q., DENG Y.F., ZHANG Z.D., Physical B, in press.
  • [15] MEKATA M., J. Phys. Soc. Jpn., 17 (1962), 796.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW7-0011-0060
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.