Consolidation and sintering of nanometric ceramic powders

• Autorzy: Zych Ł.
• Języki publikacji: EN

Abstrakty

EN

Two powders containing 97 mol % ZrO2 and 3 mol %Y2O3 with different crystallite sizes have been prepared by the hydrothermal method and calcination of co-precipitated gel. The hydrothermal powder was filter pressed under 5 MPa and dry pressed under 20 to 200 MPa. Filter pressed samples showed a more uniform particle arrangement than dry pressed samples which resulted in a better densification of the samples during sintering. Milling in water, and subsequent sedimentation of the calcinated powder allowed selecting fine particles for the filter pressing process.

Słowa kluczowe

EN

zirconia nanopowder; suspension; pressure filtration; sintering

• Wydawca: De Gruyter
• Czasopismo: Materials Science Poland
• Rocznik: 2008
• Tom: Vol. 26, No. 2
• Strony: 395--402
• Opis fizyczny: Bibliogr. 10 poz.

Twórcy

autor

Zych Ł.

• AGH University of Science and Technology, Faculty of Materials Science and Ceramics, al. Mickiewicza 30, 30-059 Cracow, Poland

Bibliografia

• [1] KINGERY W.D., FRANCOIS B., The Sintering of Crystalline Oxides. I. Interactions between Grain Boundaries and Pores, [in:] Sintering and Related Phenomena, G.C. Kuczynski, N.A. Hooton, C.F. Gibbon (Eds.), Gordon and Breach, New York, 1967, p. 471.
• [2] MAYO M.J., CHEN D-J., HAGUE D.C., Consolidation of Nanocrystalline Materials by Compaction and Sintering, [in:] Nanomaterials. Synthesis, Properties and Applications, A.S. Edelstein, R.C. Cammerata (Eds.), Institute of Physics Publ., Philadelphia, 1997, p. 165.
• [3] GAO L., LI W., WANG H.Z., ZHOU J.X., CHAO Z.J. AND ZAI Q.Z., J. Eur. Ceram. Soc., 21 (2001), 135.
• [4] DURÁN P., VILLEGAS M., CAPEL F., RECIO P., MOURE C., J. Eur. Ceram. Soc., 16 (1996), 945.
• [5] RHODES W.H., J. Am. Ceram. Soc., 64 (1981), 19.
• [6] UCHIKOSHI T., SAKKA Y., OZAWA K., HIRAGA K., J. Eur. Ceram. Soc., 18 (1998), 669.
• [7] LANGE F.F., J. Am. Ceram. Soc., 72 (1989), 3.
• [8] BUĆKO M.M., HABERKO K., FARYNA M., J. Am. Ceram. Soc., 78 (1995), 3397.
• [9] ZYCH L., HABERKO K., Solid State Phenom., 94 (2003), 157.
• [10] ZYCH L., HABERKO K., Key Eng. Mater., 264–268 (2004), 2323.