International Conference on Sol-Gel materials SGM 2001, Rokosowo, Poland
Języki publikacji
Abstrakty
In2O3:Sn (ITO) sols made of crystalline nanoparticles fully redispersable in an ethanol solution containing hydrolyzed organosilanes have been developed to get thick conducting transparent and antiglare coatings on substrates which do not withstand high temperature such as plastics (PMMA, polycarbonate) and already processed glasses. The coatings were deposited by spin, dip and spray coating processes and cured by UV irradiation and/or by a low temperature heat treatment (T = 130 °C) in air and reducing atmosphere. Their electrical, optical, textural and mechanical properties are reported. Stable sheet resistance as low as 2 kO ?was obtained with a single 500 nm thick transparent layer. Antiglare-antistatic coatings exhibiting similar sheet resistance, a gloss of 60-70 GU, a clarity of 75-90% and an optical resolution > 8 lines/mm were obtained by a room temperature spraying process. The abrasion resistance of the transparent coatings is in agreement with DIN 58196 G10 - class 1, the adhesion with DIN 58196-K2 (tape test) and the pencil hardness (ASTM D 3363-92a) is 1H.
Czasopismo
Rocznik
Tom
Strony
71--79
Opis fizyczny
Bibliogr. 13 poz.,
Twórcy
autor
autor
- Institut für Neue Materialien gem. GmbH-INM, Department of Coating Technology, Im Stadtwald, Geb. 43, 66123 Saarbruecken/Germany
Bibliografia
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPW7-0006-0008