Mathematical modeling of environment effect on fracture in materials.

• Autorzy: Andreykiv O.
• Konferencja: IV Letnia Szkoła organizowana w powiązaniuz programem TEMPUS PHARE S-JEP-11033/96. Mechanika pękania z uwzględnieniem wpływu środowiska korozyjnego. Obciążenia wieloosiowe.
• Języki publikacji: EN

Abstrakty

EN

An analysis and synthesis of the author's results on mathematical modeling of hydrogen accumulation kinetics in metals and their failure under the force and temperature factors effect has been carried out. The processes of metal hydrogenation from the gaseous phase and electrolyte as well as crack propagation during long-term static and cyclic loading and also molar hydrogen formation at the sites of its over-equilibrium concentrations in a metal are considered.

Słowa kluczowe

EN

environment; hydrogen; corrosion; adsorption; crack growth resistance; hydrogen degradation

• Wydawca: Oficyna Wydawnicza Politechniki Wrocławskiej
• Czasopismo: Prace Naukowe Instytutu Materiałoznawstwa i Mechaniki Technicznej Politechniki Wrocławskiej. Konferencje
• Rocznik: 1998
• Tom: Vol. 60, nr 8
• Strony: 91--107
• Opis fizyczny: Bibliogr. 17 poz., rys.6

Twórcy

autor

Andreykiv O.

• Karpenko Physico-Mechanical Institute, 5 Naukova Str., Lviv, Ukraine