Modification of aqueous sodium silicate solutions with morphoactive agents

• Autorzy: Stechman M. , Różycka D. , Baliński A.
• Języki publikacji: EN

Abstrakty

EN

Sodium water glass was modified with morphoactive agents added to the process of autoclave dissolving of solid water glass in water or later, during evaporative concentration of sodium silicate solution. Water dispersions of organic polymers and copolymers were used as modifiers. Modified sodium silicate solutions with SiO2/ Na2O molar ratio of 2.0 were tested as binders of moulding sands hardened with ethylene glycol diacetate. The hardened samples were tested for their technological characteristics, as: compressive strength, bending strength, tensile strength, permeability and remainder strength (W$ after baking at 100-900°C and kinetic changes of W^ value with temperature. A good effect of the modifiers chosen on technological properties of sodium silicate solutions used as binders for foundry moulding sands was stated.

Słowa kluczowe

EN

modified sodium silicate; inorganic binders in foundry

PL

modyfikacja krzemianu sodu; nieorganiczne spoiwa w odlewniach

• Wydawca: West Pomeranian University of Technology. Publishing House
• Czasopismo: Polish Journal of Chemical Technology
• Rocznik: 2003
• Tom: Vol. 5, nr 3
• Strony: 47--50
• Opis fizyczny: Bibliogr. 8 poz., rys., tab.

Twórcy

autor

Stechman M.

autor

Różycka D.

autor

Baliński A.

• Instytut Chemii Nieorganicznej, ul. Sowińskiego 11, 44-101 Gliwice, [phone], fax: [phone],,

Bibliografia

• (1) Baliński A.: Wytrzymałość resztkowa mas formierskich z uwodnionym krzemianem sodu utwardzanym dioctanem glikolu etylenowego w świetle przemian fazowych i temperaturowych powstałego żelu krzemionkowego. Archives of Mechanical Technology and Automation Polish Academy of Sciences, 2002, vol. 22, no 1, 11 - 18.
• (2) Kuckui D.: New directions in development of liquidg glass mixtures and electrophysical method for their hydraulic regeneration. 57th World Foundry Congress. Osaka 23-28.09.1990. Copyright: The Japan Foundrymen&Society, Ginza 8-12-13 Toky
• (3) Miller N. D.: Foundy binder. Pat. PCT WO 95/15229, 1995.
• (4) Pesch W., Bunte R., Beuer B.: Bindemittel auf Basis wässriger alkalimetallsilikatlösungen und deren Verwendung. EP 387682, 1995.
• (5) Różycka D., Stechman M., Wilkosz B., Baliński A.: Szkło wodne jako spoiwo w odlewnictwie. Cz. II. Struktura. Chemik 2000, 53 (8), 215 - 219.
• (6) Stechman M., Różycka D., Nowak M., Wilkosz B., Baliński A.: Szkło wodne jako spoiwo w odlewnictwie. Cz. I. Mechanizm działania i właściwości użytkowe. Chemik 2000, 53 (7), 194-197.
• (7) Stechman M., Różycka D., Legutko M.: Modyfikacja roztworów wodnych krzemianu sodu czynnikami morfoaktywnymi jej wpływ na strukturę i właściwości technologiczne mas formierskich wytwarzanych z ich udziałem. Gliwice 2002 (unpublished IChN report No. 4249.
• (8) Stechman M., Różycka D., Marszałek J., Baliński A., Szolc S M.: Otrzymywanie mas formierskich ze spoiwem w postaci krzemianów alkalicznych zawierających czynniki morfoaktywne Patent appl. IChN No. 1/2003.