The thermomechanical treatment of microalloyed steel sheets with a multiphase structure

• Autorzy: Adamczyk J. , Grajcar A.

Warianty tytułu

PL

Obróbka cieplno-mechaniczna blach o strukturze wielofazowej ze stali mikrostopowych

• Konferencja: Advanced Materials and Technologies, AMT'2004 : XVII Physical Metallurgy and Materials Science Conference (XVII; 20-24.06.2004; Łódź, Polska)
• Języki publikacji: EN

Abstrakty

EN

The chemical composition of the Nb, Ti microalloyed steel was established. The rolling and cooling conditions in the thermomechanical treatment of sheets with a ferritic - martensitic (dual phase) structure and a ferritic - bainitic with retained austenite (TRIP - Transformation Induced Plasticity) structure were determined. It was found that sheets produced according to this method have a more fine-grained structure and also better mechanical properties than after the classical underhardening or isothermal quenching from the temperature slightly higher than Acl of the investigated steel.

PL

W pracy dobrano skład chemiczny stali z mikrododatkami Nb i Ti oraz ustalono warunki walcowania metodą obróbki cieplno-mechanicznej blach o strukturze ferrytyczno - martenzytycznej (dual phase) oraz ferrytyczno - bainitycznej z austenitem szczątkowym, ulegającym przemianie martenzytycznej podczas odkształcenia technologicznego, tj. typu TRIP (Transformation Induced Plasticity). Stwierdzono, że blachy wytworzone tą metodą mają bardziej drobnoziarnistą strukturę oraz własności mechaniczne niż po klasycznym hartowaniu niezupełnym lub izotermicznym z temperatury nieco wyższej od Acl stali.

Słowa kluczowe

PL

obróbka cieplno-mechaniczna; blacha; struktura wielofazowa; stal mikrostopowa

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2004
• Tom: R. XXV, nr 3
• Strony: 498--501
• Opis fizyczny: Bibliogr. 10 poz., tab., rys.

Twórcy

autor

Adamczyk J.

• Institute of Engineering Materials and Biomaterials, Silesian University of Technology, Gliwice

autor

Grajcar A.

• Institute of Engineering Materials and Biomaterials, Silesian University of Technology, Gliwice

Bibliografia

• [1] Baumgart H., Deinzer G., Barton G.: Materiały Adam Opel AG, International Technical Development Center, Ruesselsheim (2000).
• [2] Witryna http: // www.ulsab-avc.org.
• [3] Gladman T.: The Physical Metallurgy of Microalloyed Steels. Univ. Press Cambridge, 1997.
• [4] Adamczyk J.: Inżynieria wyrobów stalowych. Wyd. Politechniki Śląskiej, Gliwice, 2000.
• [5] Sugimoto K., Lida T., Sakaguchi J., Kashima T.: ISIJ International 9 (2000)902.
• [6] Stahl far den Automobilbau, Stahlmarkt 12(1998) 38.
• [7] Bleck W., Koehler K., Meyer L., Preisendanz C.: Triyssen Tech. Ber. 23 (1991) 43.
• [8] Eberle K, Cantinieaux P., Harlet P.: Steel Research 6 (1999) 233.
• [9] Sugimoto K., Kikuchi R., Hashimoto S.: "Development of high strength low alloy TRIP-aided steels with annealed martensite matrix". Proceedings of the International Conference on TRIP-Aided High Strength Ferrous Alloys, Ghent University, Belgium, (2002) 45.
• [10] Eberle K., Cantinieaux P., Harlet P., Vande Populiere M.: I&SM 26 (1999)23.