The influence of retained austenite morphology on the impact strength of austempered Si-Mn steel

• Autorzy: Barbacki A. , Mikołajski E. , Popławski M.

Warianty tytułu

PL

Wpływ morfologii austenitu szczątkowego na udarność izotermicznie hartowanej stali Si-Mn

• Konferencja: Advanced Materials and Technologies, AMT'2004 : XVII Physical Metallurgy and Materials Science Conference (XVII; 20-24.06.2004; Łódź, Polska)
• Języki publikacji: EN

Abstrakty

EN

The application of two kinds of austenitizing, intercritical (in the alpha+gamma range) or in the austenite range, resulted in different structures as regards their morphology and retained austenite content. Subsequently to the compression test the influence of the degree of deformation on retained austenite content and hardness was measured. Austempering from intercritical range results in microstructure enabling the TRIP type effect during deformation, that is a considerable uniform deformation accompanied by strengthening. The results of impact strength tests have shown that the steel austempered from austenite range is of much higher impact strength than the intercritically austempered one. The main reason for that difference seems to be various morphology of retained austenite.

PL

Zastosowanie austenityzowania w obszarze międzykrytycznym (alfa+gamma) oraz powyżej temperatury Ac3 pozwoliło na uzyskanie zróżnicowanych struktur pod względem morfologii oraz zawartości austenitu szczątkowego (rys. 2). W próbie ściskania określono wpływ wielkości odkształcenia na zmianę zawartości austenitu szczątkowego oraz twardość (rys. 3). Austenityzowanie w obszarze międzykrytycznym umożliwia uzyskanie podczas odkształcenia efektu TRIP, to jest znaczącego wydłużenia równomiernego połączonego z umocnieniem. Badania udarności wykazały, że stal hartowana z zakresu austenitu posiada znacznie wyższą udarność niż stal po hartowaniu międzykrytycznym (tabela 2, rys. 4). Główną przyczyną tej różnicy wydaje się być inna morfologia austenitu szczątkowego.

Słowa kluczowe

PL

austenit szczątkowy; efekt TRIP; udarność; stal hartowana; morfologia

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2004
• Tom: R. XXV, nr 3
• Strony: 121--123
• Opis fizyczny: Bibliogr. 10 poz., tab., rys.

Twórcy

autor

Barbacki A.

• University of Technology, Institute of Material Science and Engineering, Poznań

autor

Mikołajski E.

• University of Technology, Institute of Material Science and Engineering, Poznań

autor

Popławski M.

• University of Technology, Institute of Material Science and Engineering, Poznań

Bibliografia

• [1] Pietrzyk J., Michta G., Osuch W., Krak A.: Stale niskowęglowez efektem TRIP. Inżynieria Materiałowa, nr 4/2002, p. 154-156.
• [2] Pacyna J., Kokoszą A., Skrzypek T.: Struktura i własności stali typuTRIP. Proc. Conf. Problemy metaloznawstwa w technice XXI wieku,Kielce - Cedzyna 2000, p. 347-354.
• [3] Sakuma Y., Matsumura O., Takechi H.: Mechanical Properties andRetained Austenite in Intercritically Heat-Treated Bainite-Transformed Steel and Their Yariation with Si and Mn Additions.Metali Trans., vol. 22A, 1991, p. 489-498.
• [4] Hanzaki A.Z., Hodgson P.D., Yue S.: The Influence of Bainite onRetained Austenite Characteristics in Si - Mn TRIP Steels, ISIJInternational, 35, 1995, p. 79-85.
• [5] Bhadeshia H.K.D.H.: Bainite In Steels, Transformations,Microstructure and Properties - Second Edition, The University Press,Cambridge 2001.
• [6] Barbacki A., Mikołajski E.: Mechanical properties and structuralstability of intercritically heated and austempered Iow alloy steels.Proc. Conf. 8* international scientific conference AMME, Rydzyna1999, p. 37-40.
• [7] Barbacki A., Mikołajski E., Głowacki Sz., Popławski M.: Wpływodkształcenia na stabilność austenitu szczątkowego w stali 35SG.Proc. Conf. XXIX Szkoła Inżynierii Materiałowej, Kraków-Wisła2001, p. 101-106.
• [8] Bhadeshia H.K.D.H., Edmonds D.V., Met. Sci., vol.!7, 1983,p.420-425.
• [9] Barbacki A., Mikołajski E., Wachowiak A.: O wpływie krzemuna strukturę i właściwości mechaniczne średniowęglowych stalipo hartowaniu bainitycznym. Inżynieria Materiałowa 2/1994, p. 33-35
• [10] Berkowski L.: Stale szybkotnące na narzędzia do obróbki plastycznej.INOP Poznań, 1994