Surface modification of unsaturated polyester resins with perfluoropolyethers

• Autorzy: Fabbri E. , Fabbri P. , Messori M. , Pilati F. , Tonelli C. , Toselli M.

Warianty tytułu

PL

Modyfikacja powierzchni nienasyconych żywic poliestrowych za pomocą poli(perfluoroeterów)

• Języki publikacji: EN

Abstrakty

EN

Fluorine-modified unsaturated polyester resins were prepared by using polycaprolactone/perfluoropolyether/polycaprolactone triblock copolymers having hydroxyl or methacrylate end-groups. Despite the immiscibility of the perfluoropolyether segment, all the modified resins were fully transparent after curing thanks to the compatibilization effect of the polycaprolactone segments. Contact angle measurements showed a very low water wettability for all investigated resin compositions. Also in the case of system with the lower bulk copolymer concentration (less than 0.3 phr) contact angle was higher than 94°. It has been demonstrated that the presence of methacrylate end-groups tends to hinder the surface segregation of the fluorinated additive.

PL

Handlową nienasyconą żywicę poliestrową modyfikowano mieszając ją z różniącymi się składem trójblokowymi kopolimerami polikaprolakton/poli(perfluoroeter)/polikaprolakton [TXCL(y)] z końcowymi grupami hydroksylowymi lub metakrylanowymi [produkt reakcji TXCL(y)Acr z metakrylanem 2-izocyjanianu etylu]. Przebieg syntezy oraz otrzymane produkty scharakteryzowano metodami FT-IR (rys. 1) i 1H NMR (tabela 1, rys. 2). Pomimo znanego braku mieszalności segmentu poli(perfluoroeteru), wszystkie modyfikowane nim żywice były przezroczyste po utwardzeniu dzięki kompatybilizującemu wpływowi segmentów polikaprolaktonu. Modyfikowane produkty charakteryzowały się bardzo małą zwilżalnością wodą (znacznie większe wartości kąta zwilżania theta niż w przypadku żywic niemodyfikowanych). Wyniki badania kąta theta (rys. 3) wskazują też, że obecność końcowych grup metakrylanowych ogranicza powodującą hydrofobowość migrację segmentów fluorowych na powierzchnię.

Słowa kluczowe

EN

unsaturated polyester resins; surface modification; polyfluoroethers; water contact angle

PL

nienasycone żywice poliestrowe; żywice poliestrowe; modyfikacja powierzchni; poli(fluoroetery); kąt zwilżania wodą

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2004
• Tom: T. 49, nr 11-12
• Strony: 785--789
• Opis fizyczny: Bibliogr. 17 poz., tab., rys.

Twórcy

autor

Fabbri E.

• Universiti di Modena e Reggio Emilia, Dipartimento di Ingegneria dei Materiali e dell' Ambiente, via Vignolese 905/A, 41100 Modena, Italy

autor

Fabbri P.

• Universiti di Modena e Reggio Emilia, Dipartimento di Ingegneria dei Materiali e dell' Ambiente, via Vignolese 905/A, 41100 Modena, Italy

autor

Messori M.

• Universiti di Modena e Reggio Emilia, Dipartimento di Ingegneria dei Materiali e dell' Ambiente, via Vignolese 905/A, 41100 Modena, Italy

autor

Pilati F.

• Universiti di Modena e Reggio Emilia, Dipartimento di Ingegneria dei Materiali e dell' Ambiente, via Vignolese 905/A, 41100 Modena, Italy

autor

Tonelli C.

• Solvay-Solexis, v. le Lombardia 20, 20021 Bollate, Italy

autor

Toselli M.

• Universita di Bologna, Departamento di Chimica Applicata e Scienza de Materiali, viale Risorgimento 2, 40136 Bologna Italy

Bibliografia

• 1. Selley J.: "Unsaturated Polyesters" in "Encyclopedia of Polymer Science and Engineering" (Ed, Mark H. F), Wiley-Interscience, New York 1988.
• 2. Kramer H.: "Polyester Resin, Unsaturated" in "UIlmann's Encyclopedia of Industrial Chemistry" (Eds. Elvers B., Hawkins S., Schulz G.), VCH publishers, 1992.
• 3. WO Pat. 01/89721 (2001).
• 4. Marais S., Metayer M., Poncin-Epaillard F: J. Fluorine Chem. 2001, 107, 199.
• 5. Marais, S., Metayer M., Labbe M., Valieton J. M., Alexandre S., Saiter J. M., Poncin-Epaillard F: Surf. Coat. Techn. 1999,122,247.
• 6. Japanese Pat. 02 16 112 (1990).
• 7. Japanese Pat. 03 234 724 (1991).
• 8. Japanese Pat. 62 98 303 (1987).
• 9. Eur. Pat. Appl. 180344 (1986).
• 10. Tonelli C, Gavezzotti P, Strepparola E.: J. Fluorine Chem. 1999,95,51,
• 11. Pilati F, Toselli M., Vallieri A, Tonelli C: Polym. Bull. 1992, 28, 151.
• 12. Toselli M., Pilati F, Fusari M., Tonelli C, Castiglioni G. J.: Appl. Polym. Sci. 1994,54,2101.
• 13. Bottino F A, Oi Pasquale G., Pollicino A., Pilati F, Toselli M., Tonelli C: Macromolecules 1998,31,7814.
• 14. Pilati F, Toselli M., Messari M., Credali U, Tonelli C, Berti C: J. Appl. Polym. Sci. 1998, 67, 1679.
• 15. Messari M., Toselli M., Pilati F, Tonelli C: Polymer 2001,42,9877.
• 16. Pilati F, Toselli M., Messari M., Priola A, Bongrovanni R., Malucelli G., Tonelli C: Macromolecules 1999,32,6969.
• 17. Toselli M., Messari M., Bongiovanni R., Malucelli G., Priola A, Pilati F, Tonelli C: Polymer 2001, 42,1771