The universal temperature parameter of rigid PVC gelation in Brabender kneader

• Autorzy: Piszczek K. , Tomaszewska J. , Sterzyński T.

Warianty tytułu

PL

Uniwersalny parametr charakteryzujący przebieg żelowania nieplastyfikowanych kompozycji PVC przetwarzanych w plastografie Brabendera

• Języki publikacji: EN

Abstrakty

EN

Course of gelation of rigid PVC Polanvil S of K-value 52, 58, 61, 67 or 70, in the chamber of Brabender kneader at temperature range 160- 185 °C and rotation speed of the rotors 10-50 min(-1), has been investigated. On the basis of torque and temperature changes as functions of process time the curves of torque changes versus real temperature of gelating blend were received. It has been observed that maximal torque value always occurred in the narrow temperature range, independently on chamber wall temperature or shear rate, and was dependent on PVC K-value. It was found that temperature related to torque maximum (T(EG)) could be universal parameter characterizing PVC gelation. The proposed new way of analysis facilitates more precise comparison of torque curves obtained at various set temperature and rotational speeds of rotors.

PL

Zbadano przebieg żelowania nieplastyfikowanych mieszanin suspensyjnego PVC "Polanvil S" o liczbie K 52, 58, 61, 67 lub 70 w komorze plastografu Brabendera w zakresie temperatury 160-185 °C i prędkości obrotowej rotorów 10-50 min(-1). Na podstawie zmian momentu obrotowego i temperatury w funkcji czasu trwania procesu (rys. 1) sporządzono krzywe zmian momentu obrotowego w funkcji rzeczywistej temperatury żelującej mieszaniny (rys. 2-4). Zaobserwowano, że maksymalna wartość momentu obrotowego występuje zawsze w wąskim zakresie temperatury, niezależnie od nastawionej wartości temperatury komory (rys. 3a) i prędkości ścinania (rys. 3b), natomiast zależy ona od liczby K przetwarzanego PVC (rys. 4). Stwierdzono, że temperatura odpowiadająca maksimum momentu obrotowego (T(EG)) może stanowić uniwersalny parametr charakteryzujący żelowanie PVC. Zaproponowany nowy sposób analizy ułatwia dokładniejsze porównanie plastogramów otrzymanych w różnych warunkach zadanej temperatury i prędkości obrotowej rotorów.

Słowa kluczowe

EN

poly(vinyl chloride); K-value; gelation; torque curve; torque maximum temperature; universal parameter

PL

poli(chlorek winylu); liczba K; żelowanie; plastogram; temperatura maksimum momentu obrotowego; parametr uniwersalny

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2004
• Tom: T. 49, nr 9
• Strony: 646--648
• Opis fizyczny: Bibliogr. 15 poz., rys.

Twórcy

autor

Piszczek K.

• University of Technology and Agriculture Faculty of Chemical Technology and Engineering, Department of Polymer Technology, ul. Seminaryjna 3, 85-326 Bydgoszcz

autor

Tomaszewska J.

• University of Technology and Agriculture Faculty of Chemical Technology and Engineering, Department of Polymer Technology, ul. Seminaryjna 3, 85-326 Bydgoszcz

autor

Sterzyński T.

• University of Technology and Agriculture Faculty of Chemical Technology and Engineering, Department of Polymer Technology, ul. Seminaryjna 3, 85-326 Bydgoszcz

Bibliografia

• 1. Bortel K, Szewczyk P.: Polimery 1993, 41, 575.
• 2. Covas J. A., Gilbert M., Marshall D. E.: PIast. Rubber. Proces. Appl. 1988,8,107.
• 3. Piszczek K, Zajchowski S., Skraga J.: Zeszyty Naukowe ATR Bydgoszcz 1986, nr 8,129.
• 4. Piszczek K, Skraga J., Zajchowski S.: Polimery 1981, 26,170.
• 5. Bambrick C. R., Hoegy L. R., Ferrari L. P.: J. Vinyl Technol. 1994,16,62.
• 6. Piszczek K, Sterzyński T., Łu~aszewicz E.: Polym. Test. 2003, 22, 11.
• 7. Pedersen T. c. J. Vinyl Technol. 1992,14,54.
• 8. Bortel K, Szewczyk P.: Polimery 1996, 44, 643.
• 9. Allsopp M. W.: in "Manufacture and Processing of PVC" (Ed. Burgess R. M.), Chapt 8., Applied Science, London 1982.
• 10. Tomaszewska J., Sterzyński T., Piszczek K: J. Appl. Polym. Sci. (will be published).
• 11. Chen C. H., Mao C. E, Lo Y. W: J. Appl. Polym. Sci. 2001, 81, 3022.
• 12. Zajchowski S., Piszczek K, Tomaszewska J.: Polimery 2001,46,236.
• 13. Piszczek K, Tomaszewska J.: Chemik 2003, nr 1, 12.
• 14. Gilbert M.: J. M. S.-Rev. Macromol. Chem. Phys. 1994, C34,77.
• 15. Schramm G.: "A practical approach to rheology and rheometry" (Polish Ed.), Poznań 1994, 215.