Thermal investigations of curing process of EPYŽ epoxy system

• Autorzy: Urbaniak M. , Grudziński K.

Warianty tytułu

PL

Badania termiczne procesu sieciowania układu epoksydowego "EPYŽ"

• Języki publikacji: EN

Abstrakty

EN

The curing, postcuring and additional postcuring of the EPYŽ epoxy system (applied for ship machine foundation chocks) have been examined by differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMTA). Parameters of curing have been determined by a dynamic variant of DSC at various heating rates. DMTA method has given an information on the epoxy system viscoelasticity. The crosslinking degree was calculated from the heat of the dynamic curing reaction. The influence of heating rate on curing parameters was shown. Glass transition temperatures of the postcured and additionally postcured epoxy systems was also determined. The results showed that the temperature range of softening of machine foundation chocks could be shifted beyond the range of their operating temperatures.

PL

Zbadano przebieg procesu utwardzania (do temp. 180 °C) w aparacie DSC (tabela 1), dotwardzania (temp. 23 °C, czas: 24,48 i 168 h - tabela 2) oraz dodatkowego dotwardzania (temp. 80 °C, czas 1 lub 2 h) układu epoksydowego "EPYŽ " ["Epidian 6" + utwardzacz (trietylenotetraamina)] z punktu widzenia jego zastosowania na podkładki fundamentowe maszyn i urządzeń okrętowych. Analizę metodą DSC procesu utwardzania prowadzono w warunkach różnej szybkości ogrzewania próbek (1, 3, 5 lub 10°C/min - rys. 1 i 2). Metodą DSC zbadano też proces dotwardzania w funkcji czasu (rys. 3). Do scharakteryzowania przebiegu procesu dotwardzania i dodatkowego dotwardzania wykorzystano metodę DMTA. Metodą tą wyznaczono wartości modułu zachowawczego (E' - rys. 4 i 5, tabele 3 i 4), współczynnika stratności (tg delta - rys. 6, tabele 3 i 4), a także temperatury zeszklenia (T(g), tabele 3 i 4). Wyniki pracy wskazują, ze samo utwardzanie (23°) nie wystarcza do uzyskania odpowiednich właściwości badanego układu epoksydowego w przedziale temperatury pracy podkładek fundamentowych (do 60 °C). Dopiero dodatkowe dotwardzanie umożliwia przesunięcie zjawiska mięknienia tych podkładek poza przedział ich temperatury roboczej.

Słowa kluczowe

EN

epoxy system; curing; postcuring; additional postcuring; dynamic mechanical properties; glass transition temperature; working temperature

PL

układ epoksydowy; utwardzanie; właściwości mechaniczne; właściwości dynamiczne; temperatura zeszklenia; temperatura pracy

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2004
• Tom: T. 49, nr 2
• Strony: 89--93
• Opis fizyczny: Bibliogr. 14 poz., tab., rys.

Twórcy

autor

Urbaniak M.

• Technical University of Szczecin Department of Mechanics and Machine Elements, Al. Piastów 19, 70-310 Szczecin

autor

Grudziński K.

• Technical University of Szczecin Department of Mechanics and Machine Elements, Al. Piastów 19, 70-310 Szczecin

Bibliografia

• 1. Karkanas P. L, Partridge L K: J. Appl. Polym. Sci. 2000,77,1419.
• 2. Penczek P., Rudnik E., Arczewska B.: Ogólnopolskie Sympozjum "Kompozyty i kompozycje polimerowe" , Szczecin 1994, p. 236.
• 3. Chiu J.: J. Macromol. Sci-Chem. 1974, A8, 3.
• 4. Wetton R. E.: "Thermal analysis" in "Polymer characterization" (ed. Hunt B. J., James M. J.), Blackie Academic & Professional, London 1993, p. 178.
• 5. Prime R. B.: "Thermosets" in "Thermal characterization of polymeric materials" (ed, Turi E. A), 2ndedition, Academic Press, London 1997, vol. 2, p. 1380.
• 6. BartonJ. M.: Adv. PoZym. Sci. 1985,72,111.
• 7. Laza J. M., Julian C. A, Larrauri E., Rodriguez M., Leon L. M.: PoZymer 1998, 40, 35.
• 8. Grudziński K, Jaroszewicz W.: Konferencja Naukowo-Techniczna "Nowe materiały - nowe technologie materiałowe w przemyśle okrętowym i maszynowym", Szczecin-Świnoujście 1998, p. 23.
• 9. Grudziński K, Jaroszewicz W.: "Posadawianie maszyn i urządzeń na podkładkach fundamentowych odlewanych z tworzywa EPY" , ZAPOL, Szczecin 2002, p. 27.
• 10. Czub P, Bończa-Tomaszewski Z., Penczek P., Pielichowski J.: "Chemia i technologia żywic epoksydowych", WNT, Warszawa 2002, p. 115.
• 11. Rosu D., Mustata E, Cascaval C. N.: Thermochim. Acta 2001,370, 105.
• 12. Rosu D., Cascaval C. N., Mustata E, Ciobanu C.: Thermochim. Acta 2002, 383, 119.
• 13. Rudnik E., Penczek P, Łazowski Z., Winiarska A: Polimery 1993,38,183.
• 14. Smith W.: "Resin chocks", Technical Paper No 2, London, Lloyds Register Technical Association, 1984-85.