Abrasive wear of concrete in hydraulic structures

• Autorzy: Horszczaruk E.

Warianty tytułu

PL

Zużycie abrazyjne betonu w konstrukcjach hydrotechnicznych

• Języki publikacji: EN

Abstrakty

EN

Abrasion wear ot concrete in hydraulic is caused by mobement of rubble carried by water, difficulties in methodology of modelling thus process in laboratory scale constitute an obstacle to the rational assessment of influence of material and environmental conditions on durability of objects exposed to these actions. This paper presents new concept of testing the abrasion of concrete by rubble carried by water, modelling the natural mechanisms pewawnr in wnvironment. It was shown, that loss of mass in abraded concrete can be expressed as function of work by the abrasive mix and a material pareameter depending on its composition and independent of the intensity of enbironment action. The results of tests allowed the criteria to be given for the selection of the composition of concrete exposed to abrasion-wear.

PL

Zużycie ścierne betonu w konstrukcjach hydrotechnicznych wywołane jest działaniem rumowiska niesionego przez wodę. Trudności metodologiczne modelowania tego procesu w skali laboratoryjnej stanowią przeszkodę racjonalnej oceny wpływu uwarunkowań materiałowych i środowiskowych na trwałość obiektów narażonych na te oddziaływania. W artykule przedstawiono nową koncepcję prowadzenia badań ścierania betonów rumowiskiem wleczonym przez wodę, modelującą naturalne mechanizmy występujące w środowisku. Wykazano, że ubytki masy ścieranych betonów wyrazić można w funkcji pracy mieszaniny ściernej oraz parametru materiałowego zależnego od jego składu i niezależnego od intensywności oddziaływania środowiska. Wyniki badań pozwoliły na określenie kryteriów doboru składu betonów narażonych na wpływy erozji ściernej.

Słowa kluczowe

EN

wear; abrasive erosion; abrasive resistance

PL

zużycie; erozja ścierna; odporność na ścieranie

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Tribologia
• Rocznik: 2003
• Tom: nr 3
• Strony: 19--35
• Opis fizyczny: Bibliogr. 19 poz., rys., tab.

Twórcy

autor

Horszczaruk E.

• Katedra Konstrukcji Żelbetowych i Technologii Betonu, Politechnika Szczecińska, Al. Piastów 50, 70-311 Szczecin

Bibliografia

• [1] Małasiewicz A.: Abrasive of concrete used in hydraulic structures at various angles of incidence on sample of rubble carried by water, Rozprawy Hydrotechniczne, PAN, Vol. 32, 1973, pp. 239-246.
• [2] Bania A.: Bestimmung des Abriebs und der Erosion von Betonen mittels eines Gesteinsstoff-Wassergemisches, Dissertation B, TH Wismar, 1989.
• [3] Bania A.: New device for testing abrasive and erosion of concrete, Ochrona przed Korozją 1991, No. 1, pp. 15-17.
• [4] Horszczaruk E.: New Test Method for Abrasive Erosion of Concrete, Kraków, 19-22 July 1996, WPK, 1996, pp. 165-174.
• [5] E. Horszczaruk, Wear of concrete due to action of aggregate and water, PhD. D. Thesis, Szczecin, pp. 31-35.
• [6] Haroske G.: Erosionsverschleiss an Betonoberflachen durch Geschiebetrans-port, Dissertation, TH Wismar, 1998, pp. 53-63.
• [7] McDonald J. E.: Evaluation of Materials for Repair of Erosion Damage in Hydraulic Structures, Durability of Concrete, Proceedings of Fifth International Conference, Barcelona, ACI, SP-192-54,2000, pp. 887-898.
• [8] Omoregie F. A., Gutschow R. A, Russel M. L.: Cement-Hardened Materials for Abrasion-erosion in Hydraulic Structures, Concrete International, 1994, No 6, pp. 47-50.
• [9] Scrivener K, Cabrion J., Letourneux R.: High-performance concretes form calcium aluminate cements, Cement and Concrete Research, Pergamon, Vol. 29, 1999, pp. 1215-1223.
• [10] Saucier F, Scrivener K., Gaudry L, Helard L: Calcium Aluminates Cement Based Concretes for Hydraulic Structures: Resistance to Erosion, Abrasive & Cavitation, Proceedings Third International Conference Under Severe Con-ditions, University of British Columbia, Vancouver, 2001, pp. 1562-1569.
• [11] Naik T. R., Singh S. S., Hossain M. M.: Abrasive Resistance of Concrete as Influenced by Inclusion of Fly Ash, Cement and Concrete Research, Vol. 24, 1994.
• [12] Naik T. R., Singh S. S., Ramme B.: Mechanical Properties and Durability of Concrete Made with Blended Fly Ash, ACI Materials Journal, Vol. 95, 1998, No. 4, 1998, pp. 454-462.
• [13] Misra A., Finnie L: On the size effect in abrasive and erosive wear, Wear 65, 1981.
• [14] Małasiewicz A.: Test systems for abrasive of hydraulic concrete, Gospodarka Wodna, 1974, No. 4, pp. 152-155.
• [15] ASTM C 418-98, Standard Test Method for Abrasive Resistance of Con-crete by Sandblasting.
• [16] Improving Z.: The Abrasive Resistance of Mortary by Adding Latex and Carbon Fibers, Cement and Concrete Research, Vol. 27, 1997, No. 8, pp. 1149-1153.
• [17] Nanni A.: Abrasive Resistance of Roller Compacted Concrete. ACT Materials Journal, Vol. 86, 1989, No. 10.
• [18] ASTM C 944-99, Standard Test Method for Abrasive Resistance of Concrete or Mortar Surfaces by the Rotating-cutter Method.
• [19] ASTM C 1138-97, Standard Test Method for Abrasive Resistance of Concrete (Underwater Method).