Effect of high temperature and load on antiwear effectiveness of zinc dialkyldithiophosphate in lubrication of partially stabilized zirconia

• Autorzy: Margielewski L. , Stanecka R. , Koralewski K.

Warianty tytułu

PL

Wpływ temperatury i obciążenia na skuteczność przeciwzużyciową dialkiloditiofosforanu cynku w smarowaniu częściowo stabilizowanego dwutlenku cyrkonu

• Języki publikacji: EN

Abstrakty

EN

The effect of high temperature and load on antiwear and antifriction effectiveness of zinc dialkyldithophosphate in lubrication of partially stabilized Zirconia were tested on ball - on - disc apparatus. Zirconia balls were used. As conterface disk made of ZrO2 partially stabilized by Y203 were applied. Synthesised ZnDTP were made from primary linear aliphatic alcohols. Tests were performed at room and higher temperatures; and at 5 to 50 N load. Investigated additives were used as pure ZnDTP and as solution in n-hexadecane. It was not found big differences in tribological performances between analysed pure ZnDTP compounds and 5% solution. It was found that the effectiveness in the reduction of friction coefficient depends on load and experiment conducting temperature.

PL

W badaniach analizowano wpływ wysokiej temperatury i siły nacisku na przeciwtarciowe właściwości dialkiloditiofosforanu cynku (ZnDTP) w ceramicznym styku tarciowym. Przeprowadzono testy na aparacie typu trzpień-tarcza, w których wykorzystano ZrO2 częściowo modyfikowany Y203, jako materiał ceramiczny tworzący styk tarciowy. Do syntezy ZnDTP użyto liniowe alkohole alifatyczne. Eksperymenty przeprowadzono w temperaturze pokojowej i wyższych, dla siły nacisku od 5 do 50 N. Badano czyste związki ZnDTP, jak również ich 5% roztwory w n-heksadekanie. Nie stwierdzono dużych różnic w działaniu przeciwtarciowym między czystym ZnDTP a jego 5% roztworem. Silą nacisku i temperatura prowadzenia testu ma istotny wpływ na własności tribologiczne analizowanych związków.

Słowa kluczowe

EN

antiwear properties; lubricant; zinc dialkyldithiophosphate additives; ceramic materials

PL

własności przeciwzużyciowe; środek smarowy; dialkiloditiofosforany cynku; materiały ceramiczne

• Wydawca: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
• Czasopismo: Tribologia
• Rocznik: 2003
• Tom: nr 2
• Strony: 55--63
• Opis fizyczny: Bibliogr. 6 poz., rys.

Twórcy

autor

Margielewski L.

• University of Lodz, Department of the Chemical Technology and Environmental Protection, Lodz, Poland

autor

Stanecka R.

• University of Lodz, Department of the Chemical Technology and Environmental Protection, Lodz, Poland

autor

Koralewski K.

• University of Lodz, Department of the Chemical Technology and Environmental Protection, Lodz, Poland

Bibliografia

• 1. Fisher T. E.: Tribochemistry of ceramic: science and applications in Plenary and Invited Papers "New Directions in Tribology", World Tribology Congress London 1997.
• 2. Gates R. S., Hsu S. M.: Effect of selected chemical compounds on the lubrication of silicon nitride. Tribology Trans., 34(1991) 417-425.
• 3. Margielewski L., Haberko K., Pedzich Z.: Influence of the Structure of Dial-kyldithiophsphates of Diffrent Metals on Tribological Behavior in Contact Steel-Zirconia.
• 4. Margielewski L., Plaza S.: Analysist of Mixtures of Dialkyldithiophosphat, Bis(dialkoxythiophosphinoyl) Disulphide and Elemental Suphur. Analyst, 17(1992), 207-210.
• 5. Plaza S., Margielewski L.: The Adsorption of the Zinc Diisobuthyldithiosphpsphates and Bis(diisobutyloxyphosphinothioyl) disulphide on Carbon Black from n-Hexadecane Solution. Tribology Trans., 36(1993) 207-212.
• 6. Plaza S.: Fizyka procesów tribologicznych, Wyd. UL, Lodz 1997.