Effect of thermochemical treatment on a selected properties of surface layer of 41CrAIMo7 steel

• Autorzy: Płonka S. , Pępek M. , Dybowski K. , Pietrasik R.
• Języki publikacji: EN

Abstrakty

EN

The paper presents tests results aimed at assessment of an effect of thermochemical treatment type, i.e. sulfonitriding and vacuum nitriding on distribution of hardness and depth of hardening, as well as microstructure of surface layer of 41CrAlMo7 machinery nitriding steel. Moreover, it was discussed an effect of the above thermochemical treatment types and successive operation of grinding with PS20 abrasive aloxite paper having grain size of 600 on geometrical structure of the surface and coefficient of kinetic friction of yarn. To make comparison with up to now state, there were also included investigations concerning the above mentioned properties of surface layer of 50SiCr4 spring steel after hardening and tempering. It has been confirmed that among investigated types of thermochemical treatments the best properties for machinery parts operated in contact with yarn were obtained in result of sulfonitriding.

PL

W artykule przedstawiono wyniki badań wpływu rodzaju obróbki cieplno-chemicznej, tj. azo-tonasiarczania i azotowania próżniowego, na rozkład twardości i głębokość utwardzenia oraz mikrostrukturę warstwy wierzchniej stali konstrukcyjnej do azotowania 41CrAlMo7. Ponadto badano wpływ tych rodzajów obróbki cieplno-chemicznej i szlifowania papierem ściernym elek-trokorundowym PS20 o wielkości ziarna 600 na chropowatość powierzchni i kinetyczny współczynnik tarcia przędzy. Dla porównania ze stanem dotychczasowym zamieszczono również badania ww. właściwości warstwy wierzchniej stali sprężynowej 50SiCr4 po hartowaniu i odpuszczaniu. Z przebadanych rodzajów obróbki cieplno-chemicznej najlepsze właściwości części maszyn współpracujących z przędzą uzyskano w wyniku zastosowania azotonasiarczania.

Słowa kluczowe

EN

sulfonitriding; vacuum nitriding; surface layer

PL

azotonasiarczanie; azotowanie próżniowe; warstwa wierzchnia

• Wydawca: Wydawnictwo Politechniki Poznańskiej
• Czasopismo: Archiwum Technologii Maszyn i Automatyzacji
• Rocznik: 2011
• Tom: Vol. 31, nr 1
• Strony: 47--56
• Opis fizyczny: Bibliogr. 11 poz.

Twórcy

autor

Płonka S.

autor

Pępek M.

autor

Dybowski K.

autor

Pietrasik R.

• Department of Manufacturing Technology and Automation, University of Bielsko-Biała, Poland

Bibliografia

• [1] ASTM D 3108-95 Standard Test Method for Coefficient of Friction, Yarn to Solid Material.
• [2] Haś Z., Kula P., The new polish nitriding and nitriding like processes in the modern technology, in: International Conference on Carburizing and Nitriding with Atmospheres, Cleveland, Ohio, 1995.
• [3] Kula P., Engineering of surface layer. Monografia, Łódź, Wydawnictwo Politechniki Łódzkiej 2000.
• [4] Nowicki B., Struktura geometryczna: chropowatość i falistość powierzchni, Warszawa, WNT 1991.
• [5] PN-EN ISO 4287:1999 Specifications of geometry of products. Geometrical structure of surface: profile method. Terms, definitions and parameters of geometrical structure of surface.
• [6] PN-81/P-04807 Testing methods of textile products. Yarn and threads. Determination of friction force and friction coefficient.
• [7] PN-82/H-04550 Thermochemical treatment. Nitrided layers. Testing.
• [8] Oczoś K.E., Liubimov V., Struktura geometryczna powierzchni, Rzeszów, Oficyna Wydawnicza Politechniki Rzeszowskiej 2003.
• [9] Płonka S., Methods of assessment and selection of optimal structure of technological process, Wydawnictwo Politechniki Łódzkiej Filia w Bielsku-Bialej 1998.
• [10] Płonka S., Hajduga M., Jędrzejczyk D., The Wear Analysis of Steel Yarn Guide in Ring Spinning Frame, Fibres & Textiles in Eastern Europe, 2007, 15, 2, p. 54-57.
• [11] Stout K.J., Blunt L., Three Dimensional Surface Topography, London, Penton Press 2000.