The influence of silicates origin on their molecular composition and properties

• Autorzy: Koźlak W.

Warianty tytułu

PL

Wpływ pochodzenia krzemianów sodowych na ich skład molekularny i właściwości

• Języki publikacji: EN

Abstrakty

EN

With methods of spectrometry based on the measurement of kinetics of the synthesis of a molibdenosilicic acid and with a specified interaction of silicates and pinacyanol chloride, spectroscopy ²⁹Si NMR, nephelometry and polymerization in the configuration: water glass and ammonium salts (IV) were studied the molecular composition and behaviour of modelled silicate samples with concentration 6m and molar ratio Na:Si equal 0,69. There were similarities and differences found in the modelled samples of sodium silicates taking also into account the industrial water glass. It has been found that the molecular composition and properties of water glass depended on the method of synthesis.

PL

Metodami spektrofotometrii opartej na pomiarze kinetyki syntezy kwasu β-molibdenokrzemowego i charakterze oddziaływania krzemianu z chlorkiem pinacyjanolu, spektroskopii ²⁹Si NMR, nefelometryczną i polimeryzacji w układzie “szkło wodne – sól ammoniowa (IV)” badano skład molekularny i zachowanie się zmodelowanych próbek krzemianów o stężeniu 6m i stosunku molowym Na:Si równym 0,69. Wykazano podobieństwa i różnice zmodelowanych próbek krzemianów sodowych uwzględniając jednocześnie szkła wodne wyjściowe (fabryczne). Ustalono, że skład molekularny i właściwości szkieł wodnych zależą od ich pochodzenia.

Słowa kluczowe

EN

sodium water glass; molecular composition; nephelometry; spectrophotometry; 29Si NMR

PL

szkło wodne sodowe; skład molekularny; nefelometria; spektrofotometria; 29Si NMR

• Wydawca: Centrum Materiałów Polimerowych i Węglowych PAN
• Czasopismo: Polish Journal of Applied Chemistry
• Rocznik: 2005
• Tom: Vol. 49, nr 3
• Strony: 227--235
• Opis fizyczny: Bibliogr. 12 poz., tabl. 2, rys. 6

Twórcy

autor

Koźlak W.

• Warsaw University of Technology, Department of Civil Engineering, Mechanics and Petrochemistry, Institute of Chemistry, 09-400 Płock, Łukasiewicza 17,

Bibliografia

• [1] W. Koźlak, Przem. Chem., 71(7), 279 (1992).
• [2] G. Engelhardt, D. Zeigan, H. Jancke, D. Hoebbel and W. Wieker, Z. Anorg. Allg. Chem., 17, 419 (1975).
• [3] D. Hoebbel, G. Garzo, G. Engelhardt and A. Till, ibid., 5, 450 (1979).
• [4] D. Hoebbel, G.Garzo,G.Engelhardt, R.Ebert and E.Lippman,M. Alla. ibid., 15, 465 (1980).
• [5] D. Hoebbel, G. Garzo, G. Engelhardt and A.Vargha, ibid., 31, 494 (1982).
• [6] D. Hoebbel and G. Engelhardt, J. Chem. Soc., Chem. Commun., 514 (1984).
• [7] D. Hoebbel and G. Engelhardt, Z. Chem., 33, 23 (1983).
• [8] R. Ebert, D. Hoebbel, R. Ohme and R. Ballschuh, Silikattechnik 198, 38 (1987).
• [9] D. Hoebbel and R. Ebert., Z Chem., 41, 28 (1988).
• [10] D. Hoebbel, R. Ebert, W. Wieker, E. Assmann and H. Mende, Z. Anorg. Allg. Chem., 471, 558 (1988).
• [11] W. Koźlak, J. Pysiak, Chem. Stos., 231, 24 (1980); 498, 28 (1984).
• [12] R. Fuchs, Berlin, AdW der DDR, Dissertation, 1969.