Chemical/electrochemical methods for the preparation of graphite multiintercalation compounds

• Autorzy: Skowroński J. M. , Urbaniak J.

Warianty tytułu

PL

Chemiczne/elektrochemiczne metody otrzymywania multiinterkalacyjnych związków grafitu

• Języki publikacji: EN

Abstrakty

EN

In this work, the process of the subsequent intercalation of HSO₄H₂SO₄ into CrO₃-GIC examined. CrO₃GICICs are prepared with two different chemical methods: this is, intercalation from the CrO₃/CH_{3COOH solution according to the Platzcr and de la Martiniere procedure and intercalation of CrO3 from Cr03/HCl solution. Furthermore, the preparation of graphite multiintercalation compound consisted with two different intercalates CrO3 and ZnCl2 from the mixture of graph ite/CrO32 HC1 was performed. The intercalation process of both intercalates CrO3 and ZnCl2 into graphite has been confirmed by cyclic voltammetric technique. Upon the successive intercalation of HSO4/H2S04 the anodic and cathodic effects characteristic for the presence of ZnCl2 and CrO3 have been served in the voltammogram. This suggests the formation of quaternary CrO3/ZnCI2-H2SO4-GIC.}

PL

Przedstawiono proces biinterkalacji Hsub>2S0₄ zachodzący w CrO₃IZG. Interkalacja CrO₃ w grafit była prowadzona z dwóch mieszanin: grafit/Cr0₃/HCl oraz grafit/CrO₃CH₃COOH. Ponadto przeprowadzono próbę jednoczesnej interkalacji dwóch interkalatów CrO₃ oraz ZnCl₂ celem otrzymania układu multiinterkalacyjnego. Aby stwierdzić czy zaszedł proces interkalacji CrO_{3 oraz ZnCl2 w grafit, produkt reakcji był badany metodą cyklicznej woltamperometrii w 95 % H2SO4. Na podstawie otrzymanych krzywych woltamperometrycznych stwierdzono obecność obu interkalatów (CrO3 oraz ZnCL2 w matrycy grafitowej. Ponadto, w wyniku anodowego utleniania CrOI3ZnCI2-IZG w 95% H2SO4 otrzymano układ poczwórny CrO3/ZnCl2H2SO4- grafit.}

Słowa kluczowe

EN

graphite intercalation compounds; intercalation; chromium trioxide; sulphuric acid

PL

związki interkalacyjne grafitu; interkalacja; trójtlenek chromu; kwas siarkowy

• Wydawca: Wydawnictwo Górnicze Sp. z o.o.
• Czasopismo: Karbo
• Rocznik: 2005
• Tom: Nr 4
• Strony: 238--243
• Opis fizyczny: Bibliogr. 11 poz.

Twórcy

autor

Skowroński J. M.

• Poznań University of Technology, Institute of Chemistry and Technical Electrochemistry, Poland

autor

Urbaniak J.

• Poznań University of Technology, Institute of Chemistry and Technical Electrochemistry, Poland

Bibliografia

• 1. Su S.R., Oblas D. W., The intercalation of micro-size graphite powder with anhydrous ferric chloride. Carbon, 1987, vol. 25, p. 391.
• 2. Stumpp E., Werner F., Graphite intercalation compounds with chlorides of manganese, nickel and zinc. Carbon, 1966, vol. 4, p. 538.
• 3. Shamsrizi M., Metz W., The System graphite/indium chloride/chlorine: threshold pressures and intercalate nucleation. Synth. Met., 1989, vol. 34 p. 91.
• 4. Bach B., Ubbelohde A. R., Chemical and electrical behaviour of graphite-metal halide compounds. J. Chem. Soc. (A), 1971, p. 3669.
• 5. Hooley J. G., Reimer M., The chromium trioxide-graphite system. Carbon, 1975, vol. 13, p. 401.
• 6. Skowroński J. M., New evidence for intercalation of graphite with CrO3. Carbon, 1989, vol. 27, p. 537.
• 7. Platzer N., de la Martinierè B., Bull. Soc. Chim. France, 1961, p. 197.
• 8. Mittal J., Konno H. and Inagaki M., Synthesis of graphite intercalation compounds with CrVI compounds using CrO3 and HCl at room temperature. Synth. Met., 1998, vol. 96, p. 103.
• 9. Besenhard J. O., Wudy E., Moehwald H., Nickl J. J., Biberacher W., Foag W., Anodic oxidation of graphite in H2SO4 dilatometry - in situ X-ray diffraction - Impedance spectroscopy. Synth. Met., 1983, vol. 7, p. 185.
• 10. Skowroński J. M., Jurewicz K., Anodic oxidation of CrO3-graphite intercalation compounds in sulfuric acid. Synth. Met., 1991, vol. 40, p. 161.
• 11. Skowroński J. M., Urbaniak J., Olejnik B., Influence of the primary ZnCl2 intercalate on electrochemical biintercalation of H2SO4 into graphite. J. Phys. Chem. Solids, 2004, vol. 65, p. 303.