Electrochemical properties of modified exfoliated graphite

• Autorzy: Skowroński J. M. , Krawczyk P.

Warianty tytułu

PL

Elektrochemiczne właściwości modyfikowanego eksfoliowanego grafitu

• Języki publikacji: EN

Abstrakty

EN

The aim of presented study was to investigate the directional dependences of elastic and optical properties of cokes produced in a laboratory scale from single initial coals of different coking properties. Cokes were produced in the Jenkner's retort furnace from 15 coals of type ranging from 33 to 37 with Roga Index (RI) in the range of 0-76. It was found that cokes exhibit the different directional properties of studied parameters. They can be divided to two groups in respect to observed differences related to the different structure of continuous matrix and to the different pores shape.

PL

Przeprowadzono badania elektrochemiczne właściwości kompozytu: eksfoliowany grafit (EG)/Ni/NiO. Stanowiący przedmiot niniejszych badań materiał kompozytowy został otrzymany w wyniku trójstopniowej syntezy. W pierwszym etapie przeprowadzono elektrochemiczną interkalacj ę kwasu siarkowego w naturalny grafit, w efekcie czego powstał interkalacyjny związek grafitu z kwasem siarkowym (H(2)SO(4)-IZG). W kolejnym etapie w wyniku elektrochemicznego osadzania niklu na H(2)SO(4)-IZG otrzymany został kompozyt H(2)SO(4)-IZG/Ni. Na drodze termicznej eksfoliacji kompozytu H(2)SO(4)-IZG/Ni otrzymano kompozyt EG/Ni/NiO. Elektrochemiczne badania kompozytu EG/Ni/NiO prowadzono w 0,5 M roztworze KOH z oraz bez dodatku 0,1 M fenolu z wykorzystaniem cyklicznej woltamperometrii. Z uzyskanych wyników wynika, że mechanizm utleniania fenolu na badanym kompozycie EG/Ni/ NiO znacznie różni się od mechanizmu, przebiegającego na eksfoliowanym graficie. Ponadto elektrochemiczna aktywność kompozytu EG/Ni/NiO bardzo wyraźnie przewyższa aktywność, jaką wykazuje oryginalny EG.

Słowa kluczowe

EN

exfoliated graphite; carbon composites; phenol oxidation

PL

grafit eksfoliowany; kompozyty węglowe; utlenianie fenolu

• Wydawca: Wydawnictwo Górnicze Sp. z o.o.
• Czasopismo: Karbo
• Rocznik: 2003
• Tom: Nr 4
• Strony: 214--217
• Opis fizyczny: Bibliogr. 14 poz.

Twórcy

autor

Skowroński J. M.

• Instytut Chemii i Elektrochemii Technicznej, Politechnika Poznańska, ul. Piotrowo 3, 60-965 Poznań
• Poznań University of Technology, Institute of Chemistry and Technical Electrochemistry, Poland

autor

Krawczyk P.

• Poznań University of Technology, Institute of Chemistry and Technical Electrochemistry, Poland

Bibliografia

• 1. Skowroński J.M., Krawczyk P., Electrochemical oxidation of phenol on exfoliated HClO₄-GIC and CrO₃-GIC in alkaline solution. Extended Abstracts, 51^th Annual Meeting of International Society of Electrochemistry. Warsaw University, 2000, p. 218.
• 2. Skowroński J.M., Krawczyk P. , Electrochemical oxidation of phenol on exfoliated graphite-based electrode. Extended Abstracts, Eurocarbon 2003, Oviedo 2003.
• 3. Russell Jr J.N., Sarvis S.S., Morris R.E., Adsorption and thermal decomposition of phenol on Ni(110). Surface Science, 1995, v. 338, p. 185.
• 4. Christoskova S.T., Stoyanova M., Degradiation of phenolic waste waters over Ni-oxide. Wat. Res., 2001, v. 35, p. 2073.
• 5. Alejandre A., Medina F., Salagre P., Fabregat A., Sueiras J.E., Characterization and activity of copper and nickel catalysts for the oxidation of phenol aqueous solutions. Appl. Catal. B. Environmental, 1998, v. 18, p. 307.
• 6. Dall'Orto V.C., Danilowicz C., Sobral S., Balbo A.L., Rezzano I., Liquid chromatography/electrochemical detection of phenols at a Poly[Ni-(Protoporphyrin IX)] chemically modified elcetrode. Anal. Chim. Acta, 1996, v. 336, p. 195.
• 7. Manriquez J., Bravo J.L., Gutierrez-Grandos S., Sucar Succar S., Bied-Charreton C., Alatorre Ordaz A., Bedioui F., Electrocatalysis of the oxidation of alcohol and phenol derivative pollutants at vitreous carbon electrode coated by nickel macrocyclic complex-based films. Anal. Chim. Acta, 1999, v. 378, p. 159.
• 8. Skowroński J.M., Krawczyk P., Matuszak J., Inagaki M., Electrochemical behaviour of nickel covered carbon spheres in alkaline solution. Extended Abstracts. Int. Symp. on Carbon, Tokio, 1998, p. 420.
• 9. Czerwiński A., Dmochowska M., Grdeń M., Kopczyk M., Wójcik G., Młynarek G., Kołata J., Skowroński J.M., Electrochemical behavior of nickel deposited on reticulated vitreous carbon. J. Power Sources, 1999, v. 77, p. 28.
• 10. Skowroński J.M., Jurewicz K., Anodic oxidation of CrO₃-graphite intercalation compounds in sulfuric acid. Synth. Met., 1991, v. 40, p. 161.
• 11. Rosłonek G., Taraszewska J., Electrocatalytic oxidation of alcohols on glassy carbon electrodes electrochemically modified with nickel tetraazamacrocyclic complexes: mechanism of film formation. J. Electroanal. Chem., 1992, v. 325, p. 285.
• 12. Skowroński J.M., Ważny A., Electrochemical oxidation of methanol on nickel foam electrode in alkaline solution. Molecular Physics Reports, 2002. v. 35. p. 49.
• 13. Block C., MacDougall B., The influence of metal oxide properties on the oxidation of organics. J. Electroanal. Chem., 2000, v. 491, p. 48.
• 14. Rivas F.J., Kolaczkowski S.T., Beltrán F.J., McLurgh D.B., Development of a model for wet air oxidation of phenol based on a free radical mechanism. Chem. Engng. Science, 1998, v. 53, p. 2575.