The paper presents the experimental results of fatigue cracks growth in the composite steel-titanium under oscillatory bending. Specimens of rectangular cross- section at a ratio of height h1: h2 = 2.5: 1 were tested. The specimens were observed fatigue crack growth parallel to the applied load, which changed the direction of the line interface. Then observed the development of cracks along the line interface or cutting through the line interface. When the crack developed along the line interface of a decline in velocity cracks. On the fractures there have been observed first of all transcrystalline cracks.
Rocznik
Tom
Strony
74--76
Opis fizyczny
Bibliogr. 3 poz.
Twórcy
autor
autor
- Politechnika Opolska, Katedra Materiałoznawstwa i Technologii Bezwiórowych, Katedra Mechaniki i Podstaw Konstrukcji Maszyn, ul. Mikołajczyka 5, PL – 45 271 Opole, r.banski@po.opole.pl
Bibliografia
- [1] POCICA A., BAŃSKI R., SZULC Z., GAŁKA A., WAINDOK P.: Badania bimetalu stal austenityczna – tytan wyżarzanego w różnych wa- runkach. Inżynieria Materiałowa. 5/2008, s. 1-4
- [2] THUM A., PETERSEN C., SWENSON O.: Verformung, Spannung und Kerbwirkung. VDI, Duesseldorf, 1960
- [3] ROZUMEK D., HEPNER M.: Wpływ mikrostruktury stopu tytanu Ti- 6Al-4V na rozwój pęknięć zmęczeniowych, Inżynieria Materiałowa, Ka- towice, 2/2005, s. 81-83
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPOK-0034-0028