Correlation between surface magnetic field and Barkhausen noise in grain-oriented electrical steel

• Autorzy: Zurek S. , Marketos P. , Tumański S. , Patel H. , Moses A.

Warianty tytułu

PL

Korelacja między powierzchniowym polem magnetycznym a szumami Barkhausena w blachach o ziarnie zorientowanym

• Języki publikacji: EN

Abstrakty

EN

Samples of 3% Si-Fe 0.27 mm thick conventional GO in a form of single strips 30 x 305 mm, cut at every 10 degrees from 0 degrees (synonymous with rolling direction) to 170 degrees were measured under sinusoidal flux density up to 1.5 T at 50 Hz and 400 Hz. The measured results show that the anisotropy of power loss and permeability is symmetrical about the rolling direction. The irregularities in the curves are caused mainly by the quality of the laser cutting and differences in the local properties of the steel sheet.

PL

Artykuł opisuje pomiary wykonane na próbkach elektrotechniczej blachy zorientowanej 3% Si-Fe pociętych w paski o wymiarach 30 x 305 x 0.27 mm pod kątami od 0 do 170 stopni (z krokiem co 10 stopni). Próbki zmierzono w warunkach sinusoidalnej indukcji do wartości 1,5 T i przy częstotliwościach 50 i 400 Hz. Wyniki wykazują, że anizotropia strat mocy i przenikalności jest symetryczna względem kierunku walcowania. Ewentualne nieregularności w zmierzonych krzywych wynikają z jakości obróbki laserowej i lokalnych własności arkusza blachy

Słowa kluczowe

EN

grain-oriented electrical steel; anisotropy; power loss; permeability

PL

zorientowana blacha elektrotechniczna; anizotropia; straty mocy; przenikalność

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Przegląd Elektrotechniczny
• Rocznik: 2009
• Tom: R. 85, nr 1
• Strony: 111--114
• Opis fizyczny: Bibliogr. 7 poz., rys., wykr.

Twórcy

autor

Zurek S.

autor

Marketos P.

autor

Tumański S.

autor

Patel H.

autor

Moses A.

• Archcliffe Road, Dover, Kent, CT17 9EN, England, United Kingdom,

Bibliografia

• [1] Dornera D., et al., Overview of microstructure and microtexture development in grain-oriented silicon steel, J. MMM 304 (2006), p. 183
• [2] Moses A.J., Konadu S.N., Some effects of grain boundaries on the field distribution on the surface of grain oriented electrical steels, Inter. J. Appl. Electromagn. Mech. 2002, Vol, 13 (1/4), p. 339
• [3] Jiles D., Introduction to Magnetism and Magnetic Materials, Chapman and Hall, NY, 1991
• [4] Mandache C., et al., Investigation of optimum field amplitude for stress dependence of magnetic Barkhausen noise, IEEE Trans. Magnetics, Vol. 43 (11), Nov 2007, p. 3976
• [5] Moses A.J., et al., Challenges in quantifying Barkhausen noise in electrical steels, Studies in Appl. Electromagn. Mech., Vol. 28, 2007, p. 178
• [6] Tumanski S., Stabrowski M., The magnetovision method as a tool to investigate the quality of electrical steel, Meas. Sci. Technol. 9 (1998), p. 488
• [7] Mohd Ali B., Moses A.J., A grain detection system for grain-oriented electrical steels, IEEE Trans. Magnetics, Vol. 25 (6), Nov. 1989, p. 4421