Asymmetry of magnetic properties of conventional grain-oriented electrical steel with relation to 2D measurements

• Autorzy: Zurek S. , Rygal R. , Soinski M.

Warianty tytułu

PL

Asymetria własności magnetycznych orientowanych blach elektrotechnicznych w warunkach przemagnesowania 2D

• Języki publikacji: EN

Abstrakty

EN

Samples of 3% Si-Fe 0.27 mm thick conventional GO in a form of single strips 30 x 305 mm, cut at every 10 degrees from 0 degrees (synonymous with rolling direction) to 170 degrees were measured under sinusoidal flux density up to 1.5 T at 50 Hz and 400 Hz. The measured results show that the anisotropy of power loss and permeability is symmetrical about the rolling direction. The irregularities in the curves are caused mainly by the quality of the laser cutting and differences in the local properties of the steel sheet.

PL

Artykuł opisuje pomiary wykonane na próbkach elektrotechniczej blachy zorientowanej 3% Si-Fe pociętych w paski o wymairach 30 x 305 x 0.27 mm pod kątami od 0 do 170 stopni (z krokiem co 10 stopni). Próbki zmierzono w warunkach sinusoidalnej indukcji do wartości 1,5 T i przy częstotliwosciach 50 i 400 Hz. Zmierzone wyniki wykazują, że anizotropia strat mocy i przenikalności jest symetryczna względem kierunku walcowania. Ewentualne nieregularności w zmierzonych krzywych wynikają z jakości obróbki laserowej i lokalnych własności arkusza blachy.

Słowa kluczowe

EN

grain-oriented electrical steel; anisotropy; power loss; permeability

PL

blacha elektrotechniczna zorientowana; anizotropia; straty mocy; przenikalność

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Przegląd Elektrotechniczny
• Rocznik: 2009
• Tom: R. 85, nr 1
• Strony: 16--19
• Opis fizyczny: Bibliogr. 10 poz., rys., wykr.

Twórcy

autor

Zurek S.

autor

Rygal R.

autor

Soinski M.

• Now at Megger Limited, Archiliffe Road, Dover, Kent CT17 9EN England,

Bibliografia

• [1] Zbroszczyk J., et al., Angular distribution of rotational hysteresis losses in Fe-3.25%Si single crystals with orientations (001) and (011), IEEE Transactions on Magnetics, Vol. Mag-17, No. 3, 1981, pp. 1975-1282
• [2] Soinski M., Angular dependencies in Fe-based commercial soft magnetic materials, IEE Proceedings-A, Vol. 139, No. 6, 1992, pp. 273-278
• [3] Gorican V., et al., Performance of round rotational single sheet tester (RRSST) at higher flux densities in the case of GO materials, Proceedings of 7th International Workshop on 1&2 Dimensional Magnetic Measurement and Testing, Ludenscheid, Germany, September 2002
• [4] Zurek S., Two-dimensional magnetisation problems in electrical steels, PhD thesis, Cardiff University, Cardiff, UK, March 2005
• [5] Zurek S., Meydan T., On the difference between clockwise and anticlockwise power losses, Part 1: Mathematical study, IEE Proceedings, Science, Measurement & Technology, Vol. 153, No. 4. July 2006, pp. 147-151
• [6] Maeda Y., et al., Rotational power losses of magnetic steel sheets in circular rotational magnetic field in ccw/cw direction, JMMM, Vol. 320 (20), Oct. 2008, pp. e567-e570
• [7] Zurek S., et al., Influence of digital resolution of measuring equipment on the accuracy of power loss measured in Epstein frame, Przegląd Elektrotechniczny, ISSN 0033-2097, 50 R. 83 NR 4/2007, pp. 50-53
• [8] Tumanski S.,Baranowski S., Magnetic sensor array for investigations of magnetic field distribution, Journal of Electrical Engineering, Vol 57. No 8/S, 2006, pp. 185-188
• [9] Zurek S., Meydan T., On the difference between clockwise and anticlockwise power losses, Part 2: Physical phenomena, IEE Proceedings, Science, Measurement & Technology, Vol. 153, No. 4. July 2006, pp. 152-157
• [10] Moses A.J., et al., Losses due to the transverse component of flux density in grain oriented electrical steels, JAPMED5, 16-19 September 2007, Larnaca, Cyprus