Study of the hot forming conditions of HSLA steel on the tensile testing machine

• Autorzy: Kozelsky P. , Melecky J. , Schindler I. , Cagala M.
• Języki publikacji: EN

Abstrakty

EN

The aim of the conducted experimental work was to study the deformation behaviour in the hot state and causes that lead to failure of compactness of a microalloyed steel determined for the tube production. The results of the formability testing are presented, performed by measurements of the strength and plastic properties by means of the tensile test performed at the forming temperatures and displacement speed of the cross beam in the range of 6 to 300 mm/min. It was shown that in the case of this material it is not essentially possible to avoid a defect formation after its cooling by a change of the forming speed.

PL

Celem przeprowadzonego eksperymentu było zbadanie technologicznej plastyczności stali HSLA w warunkach przeróbki plastycznej na gorąco, jak również przyczyn pękania stali mikroskopowych stosowanych do produkcji rur. Zaprezentowano zależność wytrzymałości i właściwości plastycznych badanej stali od warunków odkształcania. Próby rozciągania prowadzono dla temperatur z zakresu przeróbki plastycznej na gorąco tej stali z prędkością w zakresie od 6 do 300 mm/min. Wykazano, że w przypadku badanej stali zmiana prędkości kształtowania nie wpływa w istotny sposób na możliwość uniknięcia defektów po operacji chłodzenia.

Słowa kluczowe

EN

HSLA steel; tubes; hot tensile test; strength; plasticity

PL

stal HSLA; rury; próba rozciągania na gorąco; wytrzymałość; plastyczność

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Hutnik, Wiadomości Hutnicze
• Rocznik: 2008
• Tom: Vol. 75, nr 8
• Strony: 486--488

Twórcy

autor

Kozelsky P.

autor

Melecky J.

autor

Schindler I.

autor

Cagala M.

• VSB - Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic,

Bibliografia

• 1. Won Y. M., Yeo T. J., Seol D. J., Oh K. H.: A new criterion for internal crack formation in continuously cast steels, Metallurgical and Materials Transactions B, vol. 31B, no. 4, 2000, pp. 779-794B
• 2. Kim K., Oh K. H., Lee D. N.: Mechanical behavior of carbon steels during continuous casting, Scripta Materialia, vol. 34, no. 2, 1996, pp. 301-308
• 3. Chimani C. M., Resch H., Mörwald K., Kolednik O.: Precipitation and phase transformation modelling to predict surface cracks and slab quality, Ironmaking and Steelmaking, vol.32, no. 1, 2005, pp. 75-79
• 4. Kozelský P., Crha J., Havlíček F., Mazanec K.: Monitoring of Elastic-Plastic Transient Stages by Steel Using Acoustic Emission, Materials Engineering – Materiálové inžinierstvo, vol. 13, no. 3, 2006, pp. 96-99