Thermomechanical properties and chemical resistance of alkyl methacrylate/N-(4-chlorophenyl)maleimide copolymers

• Autorzy: Ryttel A.

Warianty tytułu

PL

Właściwości termomechaniczne i odporność chemiczna kopolimerów metakrylan alkilu/n-(4-chlorofenylo)maleimid

• Języki publikacji: EN

Abstrakty

EN

The copolymerizations of methyl, ethyl, butyl, pentyl, or octyl methacrylates with N-(4-chlorophenyl)maleimide [N-(4-ClPh)MI] initiated with benzoyl peroxide at the temperature range 60- 110degreesC were carried out. The content of N-(4-ClPh)MI in the initial mixtures of the monomers were 5 or 10 wt. %. N-(4- ClPh)MI was synthesized from maleic anhydride and 4- chloroaniline, in a two-step reaction. Selected properties of resulting copolymers, e.g. thermal stability, chemical resistance, Vicat softening point, T-g and hardness were determined. The influences of N-(4-ClPh)MI content in the copolymers and the length of alkyl group in methacrylates on their properties were discussed.

PL

Przeprowadzono rodnikową (wobec nadtlenku benzoilu jako inicjatora) homopolimeryzację metakrylanów metylu, etylu, butylu, pentylu i oktylu, a także ich kopolimeryzację z N-(4-chlorofenylo)maleimidem [N-(4-ClPh)MI] (5 lub 10% mas.). Otrzymane produkty scharakteryzowano metodami IR i analizy elementarnej (tabela 1). Zbadano wpływ długości łańcucha alkilowego w metakrylanie alkilu oraz obecności i zawartości N-(4-ClPh)MI w otrzymanych kopolimerach na stabilność termiczną określoną dynamiczną metodą derywato-graficzną (do 1000°C) i statyczną metodą Madorsky'ego (do 400°C) (tabela 2). Stabilność termiczną oceniano również wyznaczając temperaturę mięknienia wg Vicata (tabela 3). Stwierdzono, że N-(4-ClPh)MI zwiększa odporność termiczną kopolimerów, a także ich twardość i podwyższa temperaturę zeszklenia (tabela 3). Określono też odporność chemiczną homoi kopolimerów zarówno w różnych rozpuszczalnikach organicznych (tabela 4), jak i w różniących się stężeniem roztworach kwasów oraz zasad nieorganicznych (tabela 5). Chemiczna odporność omawianych produktów, praktycznie biorąc, nie zależy od udziału N-(4-ClPh)MI.

Słowa kluczowe

EN

copolymers; alkyl methacrylates; N-(4-chlorophenyl)maleimide; thermal stability; chemical resistance; glass transition temperature; hardness

PL

kopolimery; metakrylany alkilowe; N-(4--chlorofenylo)maleimid; stabilność termiczna; odporność chemiczna; temperatura zeszklenia; twardość

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2003
• Tom: T. 48, nr 10
• Strony: 695--700
• Opis fizyczny: Bibliogr. 25 poz.

Twórcy

autor

Ryttel A.

• Rzeszów Technical University, Faculty of chemistry, Department of Organic Chemistry, Al. Powstańców Warszawy. 35-959 Rzeszów, Poland

Bibliografia

• 1. Schildknecht E.: "Encyclopedia of Polymer Science and Engineering", Vol. 4., 2nd ed., Wiley, New York 1986, p. 779.
• 2. Leonard E. C.: "Vinyl and Diene Monomers", Part I, Wiley, New York 1970, p. 107.
• 3. Horn H. B.: "Acrylic Resins", Reinhold Publishers, New York 1960.
• 4. Dębski W.: "Polimetakrylan metylu" (in Polish), PWT, Warsaw 1969.
• 5. Van Paesschen G., Timmerman D.: Makromol. Chem. 1964, 74,112.
• 6. Coleman L. E., Conrady J. A.: J. Polym. Sci. 1959, 38, 241.
• 7. British Pat. 976 976 (1964) (CA 1965, 62,5357g).
• 8. Yamaguci K. J.: J. Polym. Sci., Chem. Ed. 1970, 8, 1427.
• 9. USA Pat. 3 676 404 (1972) {CA 1973, 78, 12 544q, 12 545r).
• 10. Hiroshi A., Masahiro K., Massanobu U., Koji T: Asahi Garasu Kogyo Gijutsu Shorekai Kenkyu Hokoku1974, 24,131 (CA 1975, 83, 97 992z).
• 11. Yamada M., Takase T., Mishima T: Kobunshi Kagaku 1967,24, 326 (CA 1968, 68, 40 127g).
• 12. USSR Pat. 166 832 (1964) (CA 1965,62, 7898q).
• 13. Yang C. R, Wang S. S.: J. Polym. Sci, Part A: Polym. Chem. 1989,27,15.
• 14. Brezdek M., Hrabak E: J. Polym. Sci., Chem. Ed. 1979, 17, 2857.
• 15. Kucharski M., Ryttel A.: Polimery 1981, 26, 381.
• 16. Ryttel A.: Acta Polymerica 1989, 40, 267.
• 17. Ryttel A.: Vie Angewandte Makromolekulare Chemie 1999, 276, 67.
• 18. Ryttel A.: J. Appl. Polym. Sci. 1999, 74, 2924.
• 19. Ryttel A.: J. Appl. Polym. Sci. 2001, 81, 3244.
• 20. Praca zbiorowa: "Preparatyka tworzyw sztucznych" (eds. Kucharski M., Lindeman ]., Malinowski J.,Rubeli T. J.) (in Polish), PWT, Warsaw 1961.
• 21. USA Pat. 2 129 690 (1938).
• 22. USA Pat. 2129 666(1938).
• 23. Ryttel A.: Zesz. Nauk. Politech. Rzeszowskiej 1989, 41(3), 41.
• 24. Madorsky S. L.: "Thermal Degradation of Organie Polymers", Wiley, New York 1964.
• 25. Polish Standard PN-78/C-89067.