AgSnBi consolidated by cyclic extrusion compression

• Autorzy: Richert M. , Richert J. , Hotloś A. , Leszczyńska-Madej B. , Maślanka M. , Mroczkowski M.

Warianty tytułu

PL

AgSnBi konsolidowany metodą cyklicznego wyciskania spęczającego

• Języki publikacji: EN

Abstrakty

EN

The work presents investigations of structure and microhardness of AgSnBi powder consolidated by cyclic extrusion compression (CEC) in the range of strains q = 0.46÷25.3, which corresponds to 1÷60 of deformation cycles. The essential decreasing of powder granules size was found after the deformation. Particles diminished from 40 um in initial powder to about 17 um after the q = 25.3. Inside powder particles subgrains/nanograins were found of about 100 nm in diameter average. The microhardness of powder strongly increases just after the first cycle of CEC, and then merely increases of about 8% from 101 to about 110 uHV after q = 25.3. The estimation of consolidation degree was evaluated by searching of cracks around the microhardness penetrator indentations inside the samples. No cracks or voids were found in the properly consolidated areas. At outer surfaces of samples contacting with tool walls some cracking were observed penetrating of about 100÷200 um inside samples.

PL

Praca przedstawia badania struktury i mikrotwardości proszku AgSnBi konsolidowanego metodą CWS w zakresie odkształceń q= 0,46÷25,3, co odpowiada 1÷60 cyklom odkształcenia. Stwierdzono istotne obniżenie się wielkości granul proszku po odkształceniu. Cząstki zmniejszyły sie od 40 ?m w proszku wyjściowym do 17 um po odkształceniu q = 25,3. Wewnątrz granul wystąpiły podziarna/nanoziarna o średniej średnicy 100 nm. Mikrotwardość proszku gwałtownie wzrosła po pierwszym cyklu odkształcenia, po czym wzrosła zaledwie o 8% od 101 do 110 uHV po odkształceniu q = 25,3. Ocenę stopnia konsolidacji przeprowadzono, poszukując pęknięć wokół odcisków mikrotwardości wewnątrz próbek. Nie znaleziono żadnych pęknięć i nieciągłości w prawidłowo skonsolidowanych obszarach. Na zewnętrznej powierzchni próbek kontaktującej się ze ściankami narzędzia obserwowano pęknięcia penetrujące w głąb próbki na głębokość 100÷200 um.

Słowa kluczowe

EN

AgSnBi powder; cyclic extrusion compression (CEC); microstructure; microhardness

PL

proszek AgSnBi; metoda cyklicznego wyciskania spęczającego CWS; mikrostruktura; mikrotwardość

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 3
• Strony: 510--513
• Opis fizyczny: Bibliogr. 10 poz., rys.

Twórcy

autor

Richert M.

autor

Richert J.

autor

Hotloś A.

autor

Leszczyńska-Madej B.

autor

Maślanka M.

autor

Mroczkowski M.

• Faculty of Non-Ferrous Metals, AGH University of Science and Technology,

Bibliografia

• [1] Findik F., Uzun H.: Microstructure, hardness and electrical properties of silver-based refractory contact materials. Materials and Design 24 (2003) 489-492.
• [2] Wua C. P, Yi D. Q., Lia J., Xiao L. R., Wang B., Zheng F.: Investigation on microstructure and performance of Ag/ZnO contact material. Journal of Alloys and Compounds 457 (2008) 565-570.
• [3] New silver-based and silver-containing materials for applications in modern areas of economy. Ed. Institute of Non-Ferrous Metals, Gliwice (2007).
• [4] Księżarek S., Besztak B.: Wires used in the production of electric contacts. Wire Journal International 40 (2000) 208-213.
• [5] US Patent 4242135: Electrical contact materials of internally oxidized Ag-Sn-Bi alloy, December 30 (1980).
• [6] Wu C. P., Yi D. Q. , Xu C. H., Li J., Wang B., Zheng F.: Microstructure of internally oxidized layer in Ag-Sn-Cu alloy. Corrosion Science 50 (2008) 3508-3518.
• [7] Richert J., Richert M.: A new method for unlimited deformation of metals and alloys. Aluminium 62 (1986) 604-607.
• [8] Richert M.: Inżynieria nanomateriałów i materiałów ultradrobnoziarnistych. Ed. Uczelniane Wydawnictwa Naukowo-Dydaktyczne AGH, Kraków (2006).
• [9] Kurzydłowski K. J., Richert M.: On the mechanisms of nanograins formation in cold plastic deformation conditions. Inżynieria Materiałowa 4 (2005) 189-193.
• [10] Valiev R. Z., Islamgaliev R. K., Alexandrov I. V.: Bulk nanostructured materials from severe plastic deformation. Progress in Materials Science 45 (2000) 103-189.