Ball milling amorphization and consolidation of NiTiZrNb and NiNbTiZrCoCu alloys

Identyfikatory
Warianty tytułu
PL
Amorfizacja i konsolidacja mielonych proszków stopów NiTiZrNb i NiNbTiZrCoCu
Języki publikacji
EN
Abstrakty
EN
Two compositions of nickel rich alloys containing Ni49.5Ti20.5Nb15Zr15 and Ni53Nb20Ti10Zr8Co5Cu3 (in at. %) were ball milled in a high energy planetary mill for 40 hours starting from pure elements. DSC measurements have shown almost complete amorphization with a high intensity exothermic crystallization peak at 590°C for the first composition and at 620°C for the second one. The X-ray diffraction confirmed amophization of milled powders showing only broad amorphous hallow. HRTEM studies allowed to identify nanocrystalline inclusions in milled powders of size below 5 nm, mostly of Ni7Ti2 phase, however in a few cases Ni30Ti9Zr or Ni2Zr phases can also be matched to a distance and mutual angles of fringes in high resolution micrographs. Hot pressing in vacuum of the amorphous powders at temperature just below crystallization allowed to consolidate powders at very low porosity below 1%. The average hardness of the first alloy was near 820 HV and that of the other one was slightly lower, however at low ductility. The HRTEM studies shown nanocrystalline particles of size up to 30 nm with the same tendency as in ball milled powders identified as nickel rich phases.
PL
Dwa stopy zawierające Ni49,5Ti20,5Nb15Zr15 i Ni53Nb20Ti10Zr8Co5Cu3 (w % at.) mielono w wysokoenergetycznym planetarnym młynku kulowym przez 40 godzin, rozpoczynając od czystych składników. Badania mikrokalorymetryczne wykazały silne maksima od krystalizacji w temperaturze odpowiednio 590°C i 620°C dla pierwszego i drugiego stopu. Badania metodą dyfrakcji rentgenowskiej potwierdziły prawie wyłączną obecność fazy amorficznej w mielonych proszkach, jakkolwiek badania metodą wysokorozdzielczej transmisyjnej mikroskopii elektronowej HRTEM pozwoliły na identyfikację cząstek nanokrystalicznych o wielkości do 5 nm fazy Ni7Ti2 oraz faz Ni30Ti9Zr lub Ni2Zr na podstawie odległości i kątów pomiędzy płaszczyznami atomowymi. Prasowanie na gorąco mielonych proszków w temperaturze poniżej krystalizacji pozwoliło na ich konsolidację przy niskiej porowatości (poniżej 1%) o twardości około 820 HV. Badania HRTEM pozwoliły na stwierdzenie wzrostu cząstek nanokrystalicznych do wielkości około 30 nm z tendencją tworzenia faz wysokoniklowych.
Rocznik
Strony
502--505
Opis fizyczny
Bibliogr. 9 poz., rys.
Twórcy
autor
autor
autor
autor
Bibliografia
  • [1] Dobromyslov A. V., Churbaev R. V., Elkin V. A. and Trenogina T. L.: Mechanical alloying of Ti-Ni alloys under high pressure. Scripta Materialia 41 (9) (1999) 1015-1021.
  • [2] Makifuchi Y., Terunuma Y., Nagumo M., Structural: Relaxtion in amorphous NiTi alloys prepared by mechanical alloying. Mater. Sci. Eng. A226-228 (1997) 312-316.
  • [3] Prokoshkin S. D., Khmelevskaya I. Yu., Dobatkin S. V., Trubitsyna I. B., Tatyanin E. V. Stolyarov V. V., Prokofiev E. A.: Alloy composition, deformation temperature, pressure and post-deformation annealing effects in severely deformed Ti-Ni based shape memory alloys. Scripta Materialia 41 (9) (1999) 1015-1021.
  • [4] Enayati M. H., Schumacher P., Cantor B.: Amorphization of Ni60Nb20Zr20 by mechanical alloying. Mater. Sci. Eng. A 375-377 (2004) 812-814.
  • [5] Shujie Pang, Tao Zhang, Asami K., Inoue A.: Bulk glassy Ni(Co-)Nb-Ti- Zr alloys with high corrosion resistance and high strength. Mater. Sci. Eng. A 375-377 (2004) 368-371.
  • [6] Pee-Yew Lee, Chung-Kwei Lin, I.-Kuan Jeng, Chien-Chung Wang, Giin- Shan Chen: Characterization of Ni57Zr20Ti18Al5 amorphous powder obtained by mechanical alloying. Materials Chemistry and Physics 84 (2004) 358-362 .
  • [7] Jei-Te Hsieh, Chung-Kwei Lin Jium-Shyong Chen, Rong-Ruey Jeng, Yu- Lom Lin, Pee-Yew Lee: Preparation and thermal stability of mechanically alloyed amorphous Ni-Zr-Ti-Si composites. Materials Science and Engineering A 375-377 (2004) 820-824.
  • [8] Oleszak D., Kulik T.: Ni59Zr20Ti16Sn5 amorphous alloy obtained by melt spinning and mechanical alloying. Journal of Non-Crystalline Solids 353 (2007) 845-847.
  • [9] Miyazaki S., Kim H., Buenconsejo P. J.: Development of high temperature Ti-Ta shape memory alloys. Proc. ESOMAT, Praha, September 7th-11th 2009 (2009) 30-38.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPL8-0015-0069
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.