Transport properties of nanocrystalline and microcrystalline Gd-doped ceria

• Autorzy: Baldinozzi G. , Dolle M. , Kusiński J. , Petot C. , Petot-Ervas G.

Warianty tytułu

PL

Właściwości transportowe nano- i monokrystalicznego dwutlenku ceru domieszkowanego gadolinem

• Języki publikacji: EN

Abstrakty

EN

Electrical conductivity measurements of Gd-doped ceria polycrystals, sintered from different sources of submicronic powder, have allowed us to illustrate the influence of size scale on the ionic conductivity. In samples doped with 10 moles % Gd2O3. The ionic conductivity passes through a maximum for grain sizes included between 200 and 500 nm. Furthermore, for the nanocrystalline samples an enhancement of the ionic conductivity is observed when the amount of dopant increases.These results were analyzed according to XPS characterizations performed on polycrystal fracture surfaces. These analysis show a grain size dependent gadolinium segregation at the periphery of the grains, which decreases with grain size, but which depends also of both densification conditions and starting powders. It follows from this set of results that the maximum of ionic conductivity occurs for a mean enrichment at the periphery of the grains close to Gd/ Ce = 0.9.

PL

Polikrystaliczne probki CeO2 domieszkowane gadolinem spiekano z różnego rodzaju mieszanin nano- i mikroproszkow. Wyniki badań uzyskanych na próbkach zawierających 10% mol. Gd2O3 pokazują, że przewodnictwo jonowe osiąga maksimum w zakresie wielkości ziarna pomiędzy 200 do 300 nm. Ponadto wykazano, że w nanokrystalicznych próbkach wzrost przewodnictwa jonowego następuje wraz ze wzrostem zawartości domieszki, podczas gdy dla materiału gruboziarnistego przewodnictwo jonowe osiąga maksimum przy 10% mol. Gd2O3. Wyjaśniono to, jako efekt wpływu wielkości ziarna proszku na segregację Gd do zewnętrznych stref ziaren, co potwierdzono badaniami za pomocą techniki XPS na przełomach próbek.

Słowa kluczowe

EN

gadolinium doped cerium oxide; electrical conductivity; XPS technique

PL

CeO2 domieszkowane gadolinem; przewodnictwo elektryczne; technika XPS

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 3
• Strony: 483--486
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Baldinozzi G.

autor

Dolle M.

autor

Kusiński J.

autor

Petot C.

autor

Petot-Ervas G.

• Ecole Centrale Paris/SRMA-CEA Saclay, France,

Bibliografia

• [1] Steele B. C. H.: Materials and engineering: The enabling technology for the commercialisation of fuell cell systems. J. Mater. Sci. 36 (2001) 1053- 1058 .
• [2] Inabe H., Tagawa H.: Ceria based electrolytes. Solid State Ionics 83 (1996) 1-16.
• [3] Suzuki T., Kosaki I., Anderson H. U.: Defect and mixed conductivity in nanocrysralline doped cerium oxides. J. Am. Cer. Soc. 85 (6) (2002) 1492- 1498.
• [4] Chiang Y. M., Lavik E. B, Kosacki I., Tuller H. L.: Nonstoichiometry and electrical conductivity of nanocrystalline ceria. J. of Electroceramics 1 (1997) 7-14.
• [5] Chiang Y. M., Lavik E. B, Blom D. A.: Defect thermodynemics and electrical conductivity properties of nanocrystalline oxides; pure and doped CeO2. NanoStructured Materials Elsevier Science 9 (1997) 633-642.
• [6] Kleinlogel C., Gaucker L. J.: Sintering and properties of nanosized ceria solid solutions. Solid State Ionics 135 (2000) 567-573.
• [7] Petot C., Filal M., Rizea A., Westmacott K. H., Laval J. Y., Lacour C.: Microstructure and ionic conductivity of freeze dried yttria-doped zirconia. J. Eur. Cer. Soc. 18 (1998) 1419-1428.
• [8] Monceau D., Petot-Ervas G., Petot C., Fraser J., Graham M. J., Sproule G. I.: Influence of the thermal treatment on themicrostructure and microchemistry of a-alumina powders doped with magnesium. J. Eur. Cer.Soc. 12 (1993) 337-341.
• [9] Chick L. A, Pederson L. R., Mopan G. D., Bates J. L., Thomas L. E., Exarhos V.: Glycine-nitrate combustion synthesis of oxide ceramic powders. J. Mater. Lett. 10 (1990) 6-12.
• [10] Rizea A., Petot C., Petot-Ervas G., Abrudeanu M., Graham M. J., Sproule, G. I.: Transport properties of yttrium-doped zirconia- Influence of kinetic demixing. Sol. St. Ionics 117 (2007) 3417-3424.