Producing and properties of the polylactide-alumina nanocomposite fibres

• Autorzy: Czarnecka P. , Ciach T. , Kunicki A. , Olszyna A. , Gołaszewska M. , Jastrzębska A.

Warianty tytułu

PL

Otrzymywanie i właściwości włókien nanokompozytu polilaktyd-tlenek glinu

• Języki publikacji: EN

Abstrakty

EN

We have described a method of producing polylactide-alumina nanocomposite fibres. Alumina nanoparticles have been combined with polylactide (PLA) to obtain composite. In the next step nanocomposite fibres have been produced by electrospinning method. Nanoalumina has been acquired by an innovative thermal decomposition method, which has been described by us earlier. The morphology and properties of the Al2O3 nanopowder as well as final product were examined using scanning electron microscope (SEM) and BET surface area measurements. Phase composition of the Al2O3 nanopowder was investigated using X-ray diffraction method. Electrospinning method allows producing homogeneous fibres of the nanocomposite PLA-Al2O3. The average particle size of the Al2O3 nanopowder incorporated in fibres was 57.9 nm. Specific BET surface area of the nanoalumina was 289.7 m2.g-1.

PL

Opisano metodę produkcji włókien nanokompozytu polilaktyd-tlenek glinu. Nanocząstki tlenku glinu połączone zostały z polilaktydem (PLA), a następnie z otrzymanego kompozytu wytworzono włókna metodą electrospinning'u. Nanotlenek glinu otrzymany został, opisaną przez autorów wcześniej, nowatorską metodą rozkładu termicznego. Morfologia i właściwości nanoproszku Al2O3, podobnie jak i produktu finalnego, przeanalizowane zostały za pomocą skaningowego mikroskopu elektronowego (SEM) oraz pomiarów powierzchni właściwej metodą BET. Skład fazowy nanoproszku Al2O3 zbadany został za pomocą dyfraktometru rentgenowskiego. Metoda electrospinning'u pozwala na wyprodukowanie homogenicznych włókien nanokompozytu PLA-Al2O3. Średnia wielkość cząstki nanoproszku Al2O3 wprowadzonego do włókien wyniosła 57,9 nm. Powierzchnia właściwa nanotlenku glinu wyniosła 289,7 m2.g-1.

Słowa kluczowe

EN

polylactide; nanoalumina; nanocomposites; fibres; electrospinning

PL

polilaktyd; nanotlenek glinu; nanokompozyty; włókna

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 3
• Strony: 467--469
• Opis fizyczny: Bibliogr. 13 poz., rys., tab.

Twórcy

autor

Czarnecka P.

autor

Ciach T.

autor

Kunicki A.

autor

Olszyna A.

autor

Gołaszewska M.

autor

Jastrzębska A.

• Faculty of Materials Science and Engineering, Warsaw University of Technology,

Bibliografia

• [1] Ciach T.: Production of electrets fibres. Master degree dissertation, Warsaw University of Technology, Faculty of Chemical Engineering (1991).
• [2] Ciach T., Gradoo L.: Highly efficient filtering materials. J. Aerosol Science 27 (1996) 613-614.
• [3] Doshi J., Reneker D.: Electrospinning process and application of electrospun fibers. J. of Electrostatics 35 (1995) 151-160.
• [4] Deitzel J. M., Kleinmeyer J., Harris D., Beck Tan N. C.: The effect of processing variables on the morphology of electrospun nanofibres and textiles. Polymer 42 (2001) 261-272.
• [5] Ciach T.: Application of electro hydro dynamic atomization in drug delivery. Journal of drug Delivery Science and Technology Editions de Sante 17 (6) (2007) 367-375.
• [6] Petrianov I. V. et al.: Fibrous filtering materials. Moscow (1968).
• [7] Filatov J.: Electro formation of fibrous materials. Moscow (1997).
• [8] Vert M., Li S. M., Spenlehauer G., Guerin, P. J.: Bioresorbility and biocomapatibility of aliphatic polyesters. Mater. Sci., Mater. Med. 3 (1992) 432-446.
• [9] Dubok V.A.: Bioceramics – yesterday, today, tomorrow. Powder Metallurgy and Metal Ceramics 39 (2000) 381-394.
• [10] Sołgała A., Kunicki A., Olszyna A.: Wpływ modyfikatora prekursora prekursora tlenku glinu na morfologię otrzymanego nanoproszku Al2O3. Materiały Ceramiczne 60 (2008) 262-265.
• [11] Jastrzębska A., Kunicki A., Olszyna A.: Obtaining and properties of nanosilver particles on nanoalumina support. Advances in Applied ceramics: Structural, Functionaland Bioceramics (in press).
• [12] Kunicki A., Olszyna A., Sołgała A.: Modyfikowane nanocząstki tlenku glinu oraz sposób otrzymywania modyfikowanych nanocząstek tlenku glinu. Zgłoszenie Nr P-386489, 10.11.2008.
• [13] Kurzydłowski K. J., ed.: The quantitative description of the microstructure of the materials. CRC Press LLC (1995).