The zinc coating solidification on surface silicon steels and DI castings

• Autorzy: Kopyciński D. , Guzik E. , Wołczyński W.

Warianty tytułu

PL

Krystalizacja powłoki cynkowej na powierzchni stali wysokokrzemowej i odlewów z żeliwa sferoidalnego

• Języki publikacji: EN

Abstrakty

EN

The studies aimed at an analysis of the formation and growth kinetics of zinc coating on reactive silicon-killed steels in a zinc bath. The growth kinetics of the produced zinc coatings was evaluated basing on the power-law growth equation. As regards galvanizing of the surface of products, investigation was done for various steel grades and ductile iron (DI) castings taking into account the quality and thickness of coating. It has been proved that the chemical constitution of basis significantly influences the kinetics of growth of the individual phases in a zinc coating. This relationship was evaluated basing on the, so called, silicon and phosphorus equivalent ESi,P and coating thickness dependences were obtained..

PL

Badania pozwoliły opisać mechanizm kształtowania powłoki cynkowej i kinetykę jej wzrostu na stalach o wysokiej zawartości krzemu i fosforu oraz na powierzchni odlewów z żeliwa sferoidalnego podczas procesu cynkowania zanurzeniowego. Kinetykę wzrostu otrzymanych powłok cynkowych oceniono przy wykorzystaniu zapisu prawa wzrostu. Przedmiotem badań były rożne gatunki stali oraz żeliwo sferoidalne, w aspekcie jakości i grubości powłoki. Wykazano, że skład chemiczny podłoża wpływa istotnie na kinetykę wzrostu poszczególnych faz powłoki cynkowej. Ocenę powyższego wpływu przeprowadzono na podstawie współczynnika ESi,P, tzw. równoważnika krzemu i fosforu.

Słowa kluczowe

EN

zinc coating; silicon-killed steels; ductile iron (DI)

PL

powłoka cynkowa; stal wysokokrzemowa; żeliwo sferoidalne

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 3
• Strony: 328--331
• Opis fizyczny: Bibliogr. 10 poz., rys., tab.

Twórcy

autor

Kopyciński D.

autor

Guzik E.

autor

Wołczyński W.

• University of Science and Technology - AGH, Kraków,

Bibliografia

• [1] Guzik E., Kopyciński D.: Steels grades for hot-dip galvanizing. Hutnik- Wiadomości Hutnicze 8-9 (2003) 348-353.
• [2] Kopyciński D., Guzik E., Wołczyński W.: The shaping of zinc coating at the surface of ductile cast iron. Inżynieria Materiałowa 5 (2006) 1081- 1084.
• [3] Kopyciński D., Guzik E.: The zinc coating on the surface ductile cast iron. Inżynieria Materiałowa, 6 (2008) 780-783.
• [4] Reumont G., Foct J., Perrot P.: New possibilities for the galvanizing process: The addition of manganese and titanium to the zinc bath. Nineteenth International Galvanizing Conference ,,Intergalva 2000”. Understanding Steel Composition and Zinc Alloys (Part 1), Berlin 2000.
• [5] Kolisnyk P. S., Allen C. J.: Galvanizing reactive steel. AGA TECH FORUM. Dallas, Texas, USA. October 12-15 (1994) 199-205.
• [6] Chen Z. W., See J. B.: Dross phases formed in galvanizing baths containing (0-0.1) wt. % nickel at 450°C. ISIJ International 33 (1993) 307-312.
• [7] Maass P., Peissker P.: Hot-dip galvanizing. Publishing Agency – Placet, Warsaw (1998).
• [8] Beguin P., Bosschaerts M., Dhaussy D., Pankert R., Gilles M.: Galveco, a solution for galvanizing reactive steel. Nineteenth International Galvanizing Conference ,,Intergalva 2000”. Understanding Steel Composition and Zinc Alloys, Berlin 2000 (2000).
• [9] Mackowiak J., Short N. R.: Metallurgy of galvanized coating. International Metals Revievs 1 (1979) 1-19.
• [10] Strutzenberger J., Faderl J.: Solidification and spangle formation of hotdip galvanized zinc coatings. Metallurgical and Materials Transactions 28A (1998) 631-642.