Laser welding of DP steel – characterization of microstructure of steel and welded joint

• Autorzy: Węglowski M. S. , Stano S. , Osuch W. , Michta G.

Warianty tytułu

PL

Spawanie laserowe stali DP – analiza mikrostruktury stali i złącza spawanego

• Języki publikacji: EN

Abstrakty

EN

In the present study, the characteristics of Nd:YAG laser welded joints of 600 MPa DP steel (HDT580X), 2.4 mm in thickness, in respect to microstructures and mechanical properties were investigated. The test joints have been welded under a shielding gas on the stand for robotic Nd:YAG laser welding. Three combinations of welding parameters were used: 2.0 kW - 2.1 m/min, 2.0 kW - 1.5 m/min and 1.5 kW - 1.2 m/min. Detailed examinations were performed on the joint welded at the highest speed. The microstructure was examined by the light, scanning (SEM) and transmission electron microscopy (TEM). The microstructure of heat affected zone (HAZ) was composed of ferrite, bainite and lath martensite, the weld contained lath martensite. The maximum hardness in the HAZ did not exceed 343 HV. The tensile strength of the welded joint was at the same level as that of the base material (630 MPa).

PL

W pracy przedstawiono wyniki badań własności mechanicznych i badań mikrostrukturalnych złączy spawanych wiązką laserową, wykonanych ze stali typu DP 600 MPa (HDT580X) o grubości 2,4 mm. Złącza zostały wykonane w osłonie gazowej na stanowisku zrobotyzowanym, wyposażonym w laser Nd:YAG. Złącza wykonano przy trzech zestawach parametrów: 2,0 kW - - 2,1 m/min, 2,0 kW - 1,5 m/min i 1,5 kW - 1,2 m/min. Szczegółowe badania mikrostrukturalne zostały przeprowadzone na złączu wykonanym z największą prędkością spawania. Badania przeprowadzono za pomocą mikroskopu świetlnego, SEM i TEM. Wyniki badań wskazują, iż SWC składa się z mieszaniny ferrytu, bainitu i martenzytu listwowego, a spoina z martenzytu listwowego. Maksymalna twardość nie przekroczyła wartości 343 HV. Wytrzymałość złączy spawanych była na tym samym poziomie, co materiału rodzimego (630 MPa).

Słowa kluczowe

EN

dual phase steel; automobile industry; laser welding; microstructure

PL

stale dual phase; przemysł samochodowy; spawanie laserowe; mikrostruktura

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 3
• Strony: 256--259
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Węglowski M. S.

autor

Stano S.

autor

Osuch W.

autor

Michta G.

• Faculty of Metals Engineering and Industrial Computer Science AGH, Kraków,

Bibliografia

• [1] Bleck W.: Cold rolled high strength sheet steels for auto applications. JOM 7 (1996) 26-31.
• [2] Davies R. G., Magee C. L.: Physical metallurgy of automotive highstrength steels. Journal of Metals 31 (1979) 17-23.
• [3] Svensson L. E., Larsson J. K.: Welding and joining of high performance car bodies. Steel World (UK) 7 (2002) 21-32.
• [4] Kang C. Y., Han T. K., Lee B. K., Kim J. K.: Characteristics of Nd:YAG laser welded 600 MPa grade TRIP and DP steel. Materials Sci. Forum 539-543 (2007) 3967-3972.
• [5] Xia M., Sreenivasan N., Lawson S., Zhou Y., Tian Z.: A comparative study of formability of diode laser welds in DP980 and HSLA steels. J. Eng. Mat. Techn. (Trans. ASME) 129 (2007) 446-452.
• [6] Krizan D., Waterschoot T., Koruk A. I., De Cooman B. C.: Bake hardening of laser welded dual phase steel. Steel Research International 74 (2004) 639-645.
• [7] Węglowski M. St., Stano S., Krasnowski K., Kwieciński K., Łomozik M., Jachym R.: The final report of statutory R&D activity. Da-104, Institute of Welding, Gliwice (2008) (in Polish).
• [8] Węglowski M., Stano S., Krasnowski K., Łomozik M., Kwieciński K., Jachym R.: Characteristics of laser welded joints of HDT580X steel. Materials Sci. Forum. 638-642 (2010) 3739-3744.
• [9] Gupta P., Ghosh P. K., Nath S. K., Ray S.: Resistance spot weldability of plain carbon and low alloy dual phase steels. Zeitschrift für Metallkunde, 81 (1990) 502-508.