Resistance to isothermal oxidation of austenitic cast steel with Ti addition

• Autorzy: Garbiak M. , Chylińska R. , Piekarski B.

Warianty tytułu

PL

Odporność na izotermiczne utlenianie staliwa austenitycznego z dodatkiem tytanu

• Języki publikacji: EN

Abstrakty

EN

Kinetics of oxidation of austenitic cast steels 30Ni-18Cr type with additions of Ti (0.03 and 0.9 wt. %) was studied. Specimens prior to oxidation were annealed at 900°C for 500 and 1000 hours. Continuous thermo-gravimetric measurements of oxidation process over 24 hrs in the air were implemented to determine the oxidation rate. Morphology and chemical composition of oxide layers was determined using X-ray diffractometry, scanning microscopy and EDS microanalysis. It has been shown that Ti additions significantly improve the oxidation resistance of these alloys and change the phase composition of the oxide layer.

PL

W pracy przedstawiono wyniki badań kinetyki utleniania staliwa austenitycznego typu 30Ni-18Cr z dodatkami Ti (0,03 i 0,93% mas.). Materiał do badań przed testem utleniania poddano procesowi wyżarzania w temperaturze 900°C przez 500 i 1000 godz. Pomiary kinetyki utleniania staliwa wykonano w atmosferze powietrza metodą termograwimetryczną ciągłą. Budowę morfologiczną i skład chemiczny warstw tlenkowych badano, wykorzystując metodę dyfrakcji rentgenowskiej, mikroskopii skaningowej oraz mikroanalizy rentgenowskiej. Wykazano, że dodatek tytanu obniża przyrost masy staliwa podczas utleniania i zmienia skład fazowy warstwy utlenionej.

Słowa kluczowe

EN

nickel-chromium cast steel; titanium addition; high temperature oxidation; scale; thermogravimetry

PL

staliwo niklowo-chromowe; dodatek tytanu; utlenianie wysokotemperaturowe; zgorzelina; termograwimetria

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 3
• Strony: 252--255
• Opis fizyczny: Bibliogr. 15 poz., rys., tab.

Twórcy

autor

Garbiak M.

autor

Chylińska R.

autor

Piekarski B.

• Institute of Materials Science and Engineering, West Pomeranian University of Technolgy, Szczecin,

Bibliografia

• [1] Heat Resistant Materials. Edited by J. R. Davis Davis & Associates, ASM Speciality Handbook, ASM International (1997).
• [2] Lai G. Y.: High-Temperature Corrosion and Materials Applications. ASM International (2007).
• [3] Saunders S. R. J., Monteiro M., Rizzo F.: The oxidation behaviour of metals and alloys at high temperatures in atmospheres containing water vapour: A review. Prog. Mater. Sci. 53 (2008) 775-837.
• [4] Nan X., Monceau D., Young D., Furtado J.: High temperature corrosion of cast heat resisting steels in Co + CO2 gas mixtures. Corr. Sci. 50 (2008) 2398-2406.
• [5] Zapała R.: Rola mikrododatków w poprawie żaroodporności staliwa odlewanego odśrodkowo. Rozprawa doktorska, AGH Kraków (2008).
• [6] Nagelberg A. S.: Oxidation of titanium modified type 310 stainless steel in low oxygen partial pressure atmosphere. Oxidation of Metals 5/6 (1982) 415-427.
• [7] Kniaginin G., Staliwo.: Metalurgia i odlewnictwo. Wydaw. Śląsk, Katowice (1977).
• [8] Chojecki A, Telejko I.: Odlewnictwo staliwa. Wydaw. Akapit, Kraków (2003).
• [9] Garbiak M., Piekarski B.: Melting of Ni-Cr cast steel with additions of niobium and titanium. Materials Science (Medžiagotyra) 11 (4) (2005) 329-333.
• [10] Garbiak M.: Wpływ niobu i tytanu na mikrostrukturę i właściwości staliwa 30Ni-18Cr. Rozprawa doktorska, Politechnika Szczecińska, Szczecin (2006).
• [11] Chylińska R., Garbiak M., Piekarski B.: Electrolytic phase extraction in stabilised austenitic cast steel. Materials Science (Medžiagotyra) 11 (4) (2005) 348-352.
• [12] Piekarski B.: Effect of Nb and Ti additions on microstructure and identification of precipitates in stabilized Ni-Cr cast austenitic steels. Mater. Char. 47/3-4 (2002) 181-186.
• [13] Chylińska R., Garbiak M., Lenart St.: Morphology of precipitates in stabilized austenitic cast steel. Mater. 13th Inter. Symp. on Metallography, Stará Lesná, Slovak Republic,02-04 May (2007) 264-267.
• [14] de Almeida L. H., Ribeiro A. F., Le May I.: Microstructural characterization of modified 25Cr-35Ni centrifugally cast steel furnace tubes. Mat. Char. 49 (2003) 219-229.
• [15] Chylińska R., Zapała R.,Garbiak M.: Mikrostruktura a odporność na izotermiczne utlenianie staliwa austenitycznego. Inżynieria Materiałowa 174 (2010) 132-136.