Influence of continuously cast bloom’s heating strategy on cracks occurence in low-alloyed Cr-Mo based steel 25CrMo4

• Autorzy: Kvicala M. , Moravka J. , Jandacka P.

Warianty tytułu

PL

Wpływ strategii grzania ciągle odlewanych kęsów na pęknięcia wewnętrzne występujące w stali niskostopowej 25CrMo4

• Języki publikacji: EN

Abstrakty

EN

In the case of the Cr-Mo based low-alloyed steel hot rolling of square billets from round continuously cast blooms is complicated by fact that internal cracks are detected during ultrasonic inspection at the end of production process on cooling bed. Final quality of hot rolled billets is influenced especially by casting speed and overheating temperature in a tundish, heating conditions in soaking pit and hot rolling factors. In our paper it is demonstrated that for optimization of heating process before hot rolling it is necessary to respect thermophysical properties of low-alloyed Cr-Mo based steels. Improved heating plan led to statistically significantly lower occurence of central cracks in hot rolled billets with minimum financial cost increase.

PL

Walcowanie bloków o przekroju kwadratowym stali Cr-Mo z ciągle odlewanych kęsów okrągłych jest komplikowane przez fakt, iż pęknięcia wewnętrzne są ujawniane dopiero podczas kontroli ultradźwiękowej na końcu całego procesu technologicznego. Na jakość wyjściową wyrobu walcowanego mają wpływ zwłaszcza prędkość odlewania, temperatura przegrzania stali w kadzi pośredniej, strategia grzania w piecu wgłębnym oraz warunki walcowania. Artykuł zwraca uwagę na fakt, iż strategia grzania przed walcowaniem musi uwzględniać właściwości termofizyczne stali niskostopowych Cr-Mo. Usprawniona strategia grzania prowadziła do znacznego zmniejszenia liczby pęknięć w wyrobach walcowanych przy minimalnym podwyższeniu kosztów.

Słowa kluczowe

EN

heating strategy; internal tension; 25CrMo4 steel; thermophysical properties

PL

strategia grzania; pęknięcia wewnętrzne; stal 25CrMo4; właściwości termofizyczne

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2010
• Tom: Vol. 31, nr 6
• Strony: 1433--1436
• Opis fizyczny: Bibliogr. 8 poz., rys., tab.

Twórcy

autor

Kvicala M.

autor

Moravka J.

autor

Jandacka P.

• Material and Metallurgical Research Ltd., Ostrava,

Bibliografia

• [1] Vazdirvanidis A., Pantazopoulos G., Louvaris A.: Failure analysis of hardened and tempered structural steel (42CrMo 4) bar for automotive applications. Engineering Failure Analysis 16 (2009) 1033÷1038.
• [2] Ghosh A.: Principles of secondary processing and casting of liquid steel. Oxford and IBH Publishing Co Pvt Ltd, New Delhi (1990).
• [3] Liška M., Raška P., Bocek D., Mušálek J., Svider R.: Výzkum, návrh a ověření technologie válcování pro zhutnění středové zóny válcovaných bloků. Závěrečná zpráva za rok 2005 úkolu TTÚ-414/A10, Ostrava, prosinec (2005).
• [4] Baker T. N.: Processes, microstructure and properties of vanadium microalloyed steels. Materials Science and Technology 25 (2009) 1083÷1107.
• [5] Rezaeian A., Zarandi F., Yue S.: Mechanism of hot ductility improvement of a peritectic steel containing vanadium using very-high-temperature compression. Metallurgical and Materials Transactions A. 39A (2008) 2644.
• [6] Mišičko R.: Cracking theories and hypothesis of continuously cast products. Acta Metallurgica Slovaka 11 (1) (2005) 116÷125.
• [7] Szturc P.: Vývoj, návrh a ověření nových technologických postupů lití a válcování ocelí na bázi Cr-Mo (pro tlakové láhve). Podkladový material pro přípravu řešení projektu – VÚ č.TTZ 429/B12, Ostrava, prosinec (2004).
• [8] Kvíčala M., Klimek M., Schindler I.: Study of technological formability of low-alloyed steel 25CrMo4. Hutnické listy 6 (2009).