Effect of forging temperature on microstructure of FeAl-based alloys

• Autorzy: Szkliniarz W. , Kościelna A.
• Konferencja: STERMAT 2008 : VIII International Conference on Stereology and Image Analysis in Materials Sciences (VIII ; 02-06.09.2008 ; Zakopane, Polska)
• Języki publikacji: EN

Abstrakty

EN

The effect of hot forging temperature on microstructure of FeAl-based alloy with chemical constitution of Fe-36Al-0.2Mo-0.05Zr-0.1C-0.02B (at. %) was characterised in this paper. The forging tests of ingots made from this alloy confirmed their deformability at a temperature of 800°C and higher, with a single draft of 80%. It was demonstrated that the deformation process was proceeding irregularly, which resulted in microstructure heterogeneity at the forging height as the zones with different recrystallisation degrees and different grain sizes. It was found that the finest grain occurred in the external zone of the forging, the intermediate - at XA of its height, while the biggest was at Vi of the forging height. The greatest microstructure recrystallisation degree was found in the external zone of the forging, while the smallest - at Vi of its height. The extremely recrystallised and refined microstructure was obtained upon forging at 800°C. Forging at higher temperature makes the microstructure recrystallisation degree in individual forging zones decrease successively and the average grain diameter increase.

PL

W pracy scharakteryzowano wpływ temperatury kucia na gorąco na mikrostrukturę stopu na osnowie fazy międzymetalicznej FeAl o składzie chemicznym Fe-36Al-0,2Mo-0,05Zr-0,lC-0,02B (% at.). Przeprowadzone próby kucia wlewków wykonanych z tego stopu potwierdziły możliwość ich odkształcania w temperaturze 800°C i wyższej z jednorazowym gniotem rzędu 80% (rys. 1). Wykazano, że proces odkształcenia przebiega w sposób nierównomierny, co skutkuje niejednorodnością mikrostruktury na wysokości odkuwki w postaci obecności stref o różnym stopniu rekrystalizacji i różnej wielkości ziarna (rys. 2-6). Stwierdzono, że najdrobniejsze ziarno występuje w strefie zewnętrznej odkuwki, pośrednie w % jej wysokości, największe w i wysokości odkuwki (rys. 7). Największy stopień rekrystalizacji mikrostruktury stwierdzono w strefie zewnętrznej odkuwki, najmniejszy w Vi jej wysokości. W największym stopniu zrekrystaUzowaną i rozdrobnioną mikrostrukturę otrzymano po kuciu w temperaturze 800°C. Kucie w wyższej temperaturze sprawia, że stopień rekrystalizacji mikrostruktury w poszczególnych strefach odkuwki sukcesywnie maleje a średnia średnica ziarna wzrasta (rys. 8).

Słowa kluczowe

PL

stop na osnowie FeAl; kucie; mikrostruktura stopu; wpływ temperatury kucia

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2008
• Tom: Vol. 29, nr 4
• Strony: 346--350
• Opis fizyczny: Bibliogr. 10 poz., rys.

Twórcy

autor

Szkliniarz W.

autor

Kościelna A.

• Department of Materials Science, Silesian University of Technology, Katowice,

Bibliografia

• [1] Stoloff N. S.: Iron aluminides: present status and future prospects, Materials Science and Engineering A258 (1998) 1-14.
• [2] Deevi S. C., Sikka V. K.: Nickel and iron aluminides: an overview on properties, processing, and applications, Intermetallics 4 (1996) 357-375.
• [3] Liu C. T., Sikka V. K., McKamey C. G.: Alloy Development of FeAl Aluminide Alloys for Structural Use in Corrosive Environments, Oak Ridge National Laboratory Report ORNL/TPM-12199, Oak Ridge, Tennessee (1993) 1-61.
• [4] Liu C. T., George E. P., Maziasz P. J., Schneibel J. H.: Recent advances in B2 iron aluminide alloys: deformation, fracture and alloy design, Materials Science and Engineering A258 (1998) 84-98.
• [5] Morris D. G., Muñoz-Morris M. A., Chao J.: Development of high strength, high ductility and high creep resistant iron aluminide, Intermetallics 12 (2004) 821-826.
• [6] Sundar R. S., Baligidad R. G., Prasad Y. V. R. K., Sastry D. H.: Processing of iron aluminides, Materials Science and Engineering A258 (1998) 219-228.
• [7] Kumar K. S., Pang L.: Effect of temperature and strain rate on the mechanical properties of Fe-40Al-0.6C, Materials Science and Engineering A258 (1998) 153-160.
• [8] Prasad Y. V. R. K., Sastry D. H., Deevi S. C.: Hot working behavior of extruded powder products of B2 iron aluminide alloys, Materials Science and Engineering A311 (2001) 42-53.
• [9] Backer I.: Recovery, recrystallization and grain growth in ordered alloys, Intermetallics 8 (2000) 1183-1196.
• [10] Skrotzki W., Kegler K., Tamm R., Oertel C.-G.: Recrystallization of Iron Aluminides, Materials Science Forum 467-470 (2004) 525-531.