Coating Zn formation during hot dip galvanizing

• Autorzy: Kopyciński D. , Guzik E. , Wołczyński W.

Warianty tytułu

PL

Kształtowanie powłoki podczas cynkowania zanurzeniowego

• Konferencja: STERMAT 2008 : VIII International Conference on Stereology and Image Analysis in Materials Sciences (VIII ; 02-06.09.2008 ; Zakopane, Polska)
• Języki publikacji: EN

Abstrakty

EN

The studies aimed at an analysis of the formation and growth kinetics of zinc coating on reactive silicon-killed steels in a zinc bath. The growth kinetics of the produced zinc coatings was evaluated basing on the power-law growth equation. As regards galvanizing of the surface of products, investigation was done for various steel grades and ductile iron taking into account the quality and thickness of coating. It has been proved that the chemical constitution of basis significantly influences the kinetics of growth of the individual phases in a zinc coating. This relationship was evaluated basing on the, so called, silicon and phosphorus equivalent E=(Si+2.5P) 103 and coating thickness dependences were obtained.

PL

Badania pozwoliły opisać mechanizm kształtowania się powłoki cynkowej i kinetykę jej wzrostu na stalach o wysokiej zawartości krzemu i fosforu oraz na powierzchni odlewów z żeliwa sferoidalnego podczas procesu cynkowania ogniowego. Kinetykę wzrostu otrzymanych powłok cynkowych oceniono przy wykorzystaniu zapisu prawa wzrostu. Przedmiotem badań były różne gatunki stali oraz żeliwo sferoidalne, w aspekcie jakości i grubości powłok. Wykazano, że skład chemiczny podłoża wpływa istotnie na kinetykę wzrostu poszczególnych faz powłoki cynkowej. Ocenę powyższego wpływu przeprowadzono na podstawie współczynnika E, tzw. równoważnik krzemu i fosforu w postaci - E= (Si+2.5P) 103.

Słowa kluczowe

PL

mechanizm kształtowania się powłoki cynkowej; proces cynkowania ogniowego; kinetyka wzrostu faz powłoki cynkowej

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2008
• Tom: Vol. 29, nr 4
• Strony: 289--292
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Kopyciński D.

autor

Guzik E.

autor

Wołczyński W.

• University of Science and Technology - AGH, Kraków,

Bibliografia

• [1] Guzik E., Kopyciński D., Miodowski Z., Winiarski M., Granatowska T.: The analysis at sorts of steels used in shipbuilding industry assigned for hot-dip galvanizing process. Ship Design and Research Center. Jubiler Scientific Conference, Gdańsk – Jurata 2001, 2 (2001) 189-200.
• [2] Reumont G., Foct J., Perrot P.: New possibilities for the galvanizing process: The addition of manganese and titanium to the zinc bath. Nineteenth International Galvanizing Conference ,,Intergalva 2000”. Understanding Steel Composition and Zinc Alloys (Part 1), Berlin (2000).
• [3] Kolisnyk P. S., Allen C. J.: Galvanizing Reactive Steel. AGA TECH FORUM. Dallas, Texas, USA. October 12-15 (1994) 199-205.
• [4] Chen Z. W., See J. B.: Dross Phases Formed in Galvanizing Baths Containing (0-0.1) wt. % nickel at 450°C, ISIJ International 33 (1993) 307-312.
• [5] Maass P., Peissker P.: Hot-dip galvanizing. Publishing Agency - Placet. Warsaw (1998).
• [6] Beguin P., Bosschaerts M., Dhaussy D., Pankert R., Gilles M.: Galveco, a solution for galvanizing reactive steel. Nineteenth International Galvanizing Conference ,,Intergalva 2000”. Understanding Steel Composition and Zinc Alloys (Part 1), Berlin (2000).
• [7] Mackowiak J., Short N. R.: Metallurgy of galvanized coating. International Metals Revievs 1 (1979) 1-19.
• [8] Fraś E.: Crystallization of Metals, WNT, Warsaw (2003).
• [9] Strutzenberger J., Faderl J.: Solidification and spangle formation of hotdip galvanized zinc coatings, Met. and Mater. Trans. A 28A (1998) 631- 642