Application of quantitative profile analysis in the assessment of hydrogen embrittlement of duplex stainless steel

• Autorzy: Michalska J.

Warianty tytułu

PL

Zastosowanie ilościowej oceny profili w ocenie niszczenia wodorowego stali typu duplex

• Konferencja: STERMAT 2008 : VIII International Conference on Stereology and Image Analysis in Materials Sciences (VIII ; 02-06.09.2008 ; Zakopane, Polska)
• Języki publikacji: EN

Abstrakty

EN

A variety of effects provoked by the presence of hydrogen in materials used in complex conditions of mechanical loading, heat burden and corrosion require the application of many modern research methods. For this purpose, fractographic methods may be particularly useful, especially quantitative characteristics of fracture surfaces. The paper presents the results of studies concerning the mechanical and fractographical investigations of 2205 duplex stainless steel after hydrogen charging. It has been proved that the quantitative evaluation of hydrogen cracking phenomenon is possible thanks to a set of quantitative fractography parameters, which comprises fracture linear roughness, overlap coefficient and the phase dominance factor.

PL

Różnorodność zjawisk prowokowanych obecnością wodoru w materiałach stosowanych w warunkach złożonych obciążeń mechanicznych, cieplnych i korozyjnych wymaga zastosowania wielu nowoczesnych metod badawczych. Zastosowanie metod fraktograficznych może być szczególnie użyteczne w tym celu, zwłaszcza ilościowy opis przełomów. W pracy przedstawiono wyniki badań mechanicznych i fraktograficznych dla stali duplex 2205 po nawodorowaniu katodowym. Wykazano, że ilościowa ocena zjawiska kruchości wodorowej jest możliwa w oparciu o zestaw ilościowych parametrów fraktograficznych, takich jak: współczynnik rozwinięcia profilu, wymiar fraktalny, udział przesłonięć na profilu i współczynnik dominacji fazy na profilu.

Słowa kluczowe

PL

stal duplex 2205; badania mechaniczne; badania fraktograficzne; niszczenie wodorowe

• Wydawca: Wydawnictwo SIGMA-NOT
• Czasopismo: Inżynieria Materiałowa
• Rocznik: 2008
• Tom: Vol. 29, nr 4
• Strony: 185--187
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Michalska J.

• Silesian University of Technology, Katowice,

Bibliografia

• [1] Luu W. C., Liu P. W., Wu J. K.: Hydrogen transport and degradation of a commercial duplex stainless steel, Corrosion Science 44 (2002) 1783- 1791.
• [2] Young S. C., Chan S. L. L., Tsay L. W., Shin C. S.: Hydrogen-enhanced cracking of 2205 duplex stainless steel welds, Materials Chemistry and Physics 91 (2005) 21-25.
• [3] Lemaitre C.: Corrosion sous contrainte: Methods d’essais, “Corrosion sous contrainte, Phénoménologies et Mécanismes “, Ed. Scientif. D. Desjardins et R. Oltra, Bombannes (1990) 467-488.
• [4] ASTM G129-00: Standard Practice for Slow Strain Rate Testin to Evaluate the susceptibility of Metallic Materials to Environmentally Assisted Cracking.
• [5] Szala J.: PROFIL, authorized program, Department of Materials Science, Silesian University of Technology, Katowice, Poland.
• [6] Szala J.: ANALYSIS OF PROFIL, authorized program, version 2.2, Department of Materials Science, Silesian University of Technology, Katowice, Poland.
• [7] Ryś J.: Stereologia materiałów, Kraków, Fotobit (1995).
• [8] Michalska J.: The assessment of hydrogen embrittlement resistance of duplex stainless steel, PhD thesis, Silesian University of Technology, Katowice, Poland, (2006).
• [9] Sozańska M., Sojka J., Betáková P., Dagbert C., Hyspecká L., Galland J., Tvyrdý J.: Examination of hydrogen interaction in carbon steel by means of quantitative microstructural and fracture descriptions, Materiale Characterization 46 (2001) 239-243.