Epoxy-carbazole compositions. Part I. Compositions with 9-(2, 3-epoxypropyl) carbazole

• Autorzy: Czub P. , Mazela W. , Pielichowski J.

Warianty tytułu

PL

Kompozycje epoksydowo-karbazolowe. Cz. I. Kompozycje z 9-(2,3-epoksy-propylo)karbazolem

• Języki publikacji: EN

Abstrakty

EN

Compositions of low-molecular weight epoxy resin Ruetapox 0162 mixed with various amounts of 9-(2,3-epoxypropyl)carbazole (EPK) have been prepared and cured by isophorone diamine. Mechanical, thermal and photoluminescence properties of obtained materials were determined. It was found that low- molecular weight epoxy resin is an excellent dispersing matrix for carbazole groups, which secures suitable mechanical properties, low combustibility and high thermal stability of prepared materials. Moreover, it was observed that the addition of 10 wt. % of EPK improves compression strength by 15%, flexural strength by 33% and also slightly decreases water absorption. Thin film forming ability and optic properties, characteristic for isolated carbazole molecules (photoluminescence maxima at 352 and 368 nm), point at the possibility to use studied materials for light-emitting diodes (LED) construction.

PL

W wyniku mechanicznego zmieszania otrzymano jednorodne kompozycje małocząsteczkowej żywicy epoksydowej (diglicydy-lowego eteru bisfenolu A) o różnej zawartości (5, 10 i 15% mas.) 9-(2,3-epoksypropylo)karbazolu (EPK). Kompozycje te następnie sieciowano izoforonodiaminą i badano ich właściwości mechaniczne, termiczne oraz fotoluminescencyjne. Stwierdzono, że malocząsteczkowa żywica epoksydowa doskonale spełnia rolę matrycy rozpraszającej grupy karbazolowc, co nadaje otrzymanym materiałom korzystną charakterystykę mechaniczną, małą palność i dużą odporność termiczną (tab. 1 i 2). Optymalne właściwości wykazują kompozycje zawierające 10% mas. EPK. Łatwość formowania cienkich warstw oraz właściwości optyczne charakterystyczne dla izolowanych cząsteczek karbazolu (z maksimami fotoluminescencji przy 353 i 368 nm) (rys. 2) wskazują na możliwość zastosowania badanych kompozycji jako materiałów do konstrukcji diod świecących.

Słowa kluczowe

EN

epoxy resins; 9-(2;3-epoxypropyl)carbazole; light-emitting diodes; mechanical properties; thermal properties; photoluminescence properties

PL

żywice epoksydowe; 9-(2,3-epoksypropylo)karbazol; diody świecące; właściwości mechaniczne; właściwości termiczne; właściwości fotoluminescencyjne

• Wydawca: Sieć Badawcza Łukasiewicz – Instytut Chemii Przemysłowej
• Czasopismo: Polimery
• Rocznik: 2003
• Tom: T. 48, nr 9
• Strony: 641--644
• Opis fizyczny: Bibliogr. 16 poz.

Twórcy

autor

Czub P.

• Cracow University of Technology, Independent Department of Chemistry and Technology of Polymers, ul. Warszawska 24, 31-155 Kraków, Poland

autor

Mazela W.

• Cracow University of Technology, Independent Department of Chemistry and Technology of Polymers, ul. Warszawska 24, 31-155 Kraków, Poland

autor

Pielichowski J.

• Cracow University of Technology, Independent Department of Chemistry and Technology of Polymers, ul. Warszawska 24, 31-155 Kraków, Poland

Bibliografia

• 1. Akhmedov Kh. M., Karomiv Kh. S., Shcherbakova I. M., Porshev Yu. M., Cherkashin M. I.: Usp. Khim. 1990,59,738, (English translation in: Russ. Chem. Rev. 1990, 59(5), 425).
• 2. Romero D. B., Schaer M., Leclerc M., Ades D., Siove A., Zuppiroli L. Z.: Synth. Met. 1996, 80, 271.
• 3. Tamulaitis G., Gulbinas V, Undzenas A., Valkunas L: J. Lumin. 1999, 82, 327.
• 4. Sun R. G., Wang Y. Z., Wang D. K., Zheng Q. B., Epstein A. J.: Synth. Met. 2000, 111—112, 403.
• 5. Kim D. Y, Cho H. N., Kim C. Y: Prog. Polym. Sci. 2000, 25, 1089.
• 6. Stephan O., Vial J.-C.: Synth. Met. 1999,106,115.
• 7. Shim H.-K., Kim H.-J., Ahn T., Kang I.-N., Zyung T: Synth. Met. 1997 ,91, 289.
• 8. Bogda! D., Warzała M., Pielichowski J., Sanetra J.: Polimery 1999, 44, 146.
• 9. Zheng H., Zhang R., Wu F., Tian W., Shen J.: Synth.Met. 1999,100,291.
• 10. Jin S.-H., Kim W.-H., Song I.-S., Kwon S.-К., Lee К.-S., Han E.-M.: Thin Solid Films 2000, 363, 255.
• 11. Abe S. Y, Bernede J. C., Delvalle M. A., Tregouet Y., Ragot F., Diaz F. R., Lefrant S.: Synth. Met. 2002, 126,1.
• 12. Bogdal D., Yashchuk V., Pielichowski J., Stępień I., Ogul'chansky T, Warzala M., Kudrya V: Polimery 2002,47,279.
• 13. Czub R, Mazela W., Pielichowski J.: Materials (S-5/P-70) of The Polish Chemical Society XLIII Annual Conference, Łódź 10—15.09.2000.
• 14. Mazela W., Czub P, Pielichowski J.: Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej 2001, 50(23), 446.
• 15. Mazela W., Pielichowski J., Czub P, Sanetra J.: Prace Naukowe Instytutu Technologii Organicznej i Tworzyw Sztucznych Politechniki Wrocławskiej 2001,50(23), 400.
• 16. Sanetra J.: Fizyczne właściwości układów polimerowych zawierających grupę karbazolową w aspekcie zastosowania ich w diodach elektroluminescencyjnych, Zeszyty Naukowe Politechniki Krakowskiej, Podstawowe Nauki Techniczne, 2001, No. 33.